Tensile Properties of Open Cell Ceramic Foams
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00322731" target="_blank" >RIV/68081723:_____/09:00322731 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/09:PU85855
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Tensile Properties of Open Cell Ceramic Foams
Popis výsledku v původním jazyce
Full understanding of response of highly porous (cellular) ceramic foams to different mechanical loading conditions is important because of their potential use in industry, medical and other applications. Technique of tensile test of ceramic foam materials has been developed and first knowledge is described in the paper. Tested material was based on alumina ceramic; it was manufactured by slurry coating of polyurethane foam. Two cell sizes were included into the study 10 and 60 PPI. Testing procedure consists from fixation of ceramic foam into aluminium pots by suitable adhesive. Tensile test results generated using two specimen sizes with cross-section 10x10 and 15x15 mm have been statistically analysed. Basic fractographic analysis was applied to getcorresponding figure about specimens behaviour during tensile loading.
Název v anglickém jazyce
Tensile Properties of Open Cell Ceramic Foams
Popis výsledku anglicky
Full understanding of response of highly porous (cellular) ceramic foams to different mechanical loading conditions is important because of their potential use in industry, medical and other applications. Technique of tensile test of ceramic foam materials has been developed and first knowledge is described in the paper. Tested material was based on alumina ceramic; it was manufactured by slurry coating of polyurethane foam. Two cell sizes were included into the study 10 and 60 PPI. Testing procedure consists from fixation of ceramic foam into aluminium pots by suitable adhesive. Tensile test results generated using two specimen sizes with cross-section 10x10 and 15x15 mm have been statistically analysed. Basic fractographic analysis was applied to getcorresponding figure about specimens behaviour during tensile loading.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials
ISSN
1013-9826
e-ISSN
—
Svazek periodika
409
Číslo periodika v rámci svazku
-
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
8
Strana od-do
—
Kód UT WoS článku
000269684800018
EID výsledku v databázi Scopus
—