Behaviour of Open Cell Ceramic Foams in Tension
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00366275" target="_blank" >RIV/68081723:_____/11:00366275 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Behaviour of Open Cell Ceramic Foams in Tension
Popis výsledku v původním jazyce
Full understanding of response of highly porous (cellular) ceramic foams to different mechanical loading conditions is important because of their potential use in industry, medical and other applications. Technique of tensile test of ceramic foam materials has been developed and first knowledge is described in the paper. Tested material was based on alumina ceramic; it was manufactured by slurry coating of polyurethane foam. Two cell sizes were included into the study 10 and 60 PPI. Testing procedure consists from fixation of ceramic foam into aluminium pots by suitable adhesive. Tensile test results generated using two specimen sizes with cross-section 10x10 and 15x15 mm have been statistically analysed. Basic fractographic analysis was applied to getcorresponding figure about specimens behaviour during tensile loading.
Název v anglickém jazyce
Behaviour of Open Cell Ceramic Foams in Tension
Popis výsledku anglicky
Full understanding of response of highly porous (cellular) ceramic foams to different mechanical loading conditions is important because of their potential use in industry, medical and other applications. Technique of tensile test of ceramic foam materials has been developed and first knowledge is described in the paper. Tested material was based on alumina ceramic; it was manufactured by slurry coating of polyurethane foam. Two cell sizes were included into the study 10 and 60 PPI. Testing procedure consists from fixation of ceramic foam into aluminium pots by suitable adhesive. Tensile test results generated using two specimen sizes with cross-section 10x10 and 15x15 mm have been statistically analysed. Basic fractographic analysis was applied to getcorresponding figure about specimens behaviour during tensile loading.
Klasifikace
Druh
O - Ostatní výsledky
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA101%2F09%2F1821" target="_blank" >GA101/09/1821: Mechanické a lomové vlastnosti multilamelárních struktur typu keramika/keramika a keramika/kov s gradientními vrstvami</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů