Analysis of elements redistribution in Ni-coated ferritic steel for molten salts technologies

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00326256" target="_blank" >RIV/68081723:_____/09:00326256 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of elements redistribution in Ni-coated ferritic steel for molten salts technologies

Popis výsledku v původním jazyce

Changes in structure and chemical composition of Ni-coated ferritic steel ČSN 411523 are studied in the present paper. The Ni-coated material is perspective for applications in molten salts technologies. The samples were subjected to corrosion in moltenmixture 60 mol. % LiF + 40 mol. % NaF at temperature 953 K, the duration exposition was 100, 300 and 1000 h. Experiments were carried out in a quasidynamic regime simulating the flow of the cooling media (the mixture of molten salts) in the pipeline system. The change of chemical composition in the vicinity of interface between the Ni layer and steel substrate was measured by SEM.

Název v anglickém jazyce

Analysis of elements redistribution in Ni-coated ferritic steel for molten salts technologies

Popis výsledku anglicky

Changes in structure and chemical composition of Ni-coated ferritic steel ČSN 411523 are studied in the present paper. The Ni-coated material is perspective for applications in molten salts technologies. The samples were subjected to corrosion in moltenmixture 60 mol. % LiF + 40 mol. % NaF at temperature 953 K, the duration exposition was 100, 300 and 1000 h. Experiments were carried out in a quasidynamic regime simulating the flow of the cooling media (the mixture of molten salts) in the pipeline system. The change of chemical composition in the vicinity of interface between the Ni layer and steel substrate was measured by SEM.

Druh

D - Stať ve sborníku

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

<a href="/cs/project/2A-1TP1%2F067" target="_blank" >2A-1TP1/067: Výzkum technologií pro přenos vysokopotencionálního tepla z jaderného zdroje.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metal 2009. Conference Proceedings

ISBN

978-80-87294-04-8

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Tanger s. r. o

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí

Datum konání akce

19. 5. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000269313300036