Strukturní změny ve dvou vybraných kovových materiálech po expozici v roztavené eutektické směso LiF-NaF - model korozního chování

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00324374" target="_blank" >RIV/68081723:_____/09:00324374 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structure changes in two chosen metallic materials exposed to molten LiF-NaF eutectic mixture ? model of corrosion behaviour

Popis výsledku v původním jazyce

This work is devoted to the study of changes of structure and chemical composition of two candidate materials for high-temperature power engineering. Materials are studied before and after their exposure to molten mixture 60 mol.% LiF + 40 mol.% NaF at temperature 953 K for exposure times 100, 300 and 1000 h. The exposition was carried out in a quasidynamic regime that simulated the flux of the coolant (the mixture of salts) in the pipeline. In Ni-alloy Ni-6 W-9 Mo-1.7 Ti-7 Cr (wt.%) severe corrosion damage was observed in the surface layer of thickness of about 100 ?m. In Ni-coated ferrite steel CSN 411523, elements redistribution close to the interface between the Ni layer/steel substrate was described by a simple model. The Ni layer showed excellentresistance against the corrosion, but its perforation and subsequent local damage of the substrate were also observed.

Název v anglickém jazyce

Structure changes in two chosen metallic materials exposed to molten LiF-NaF eutectic mixture ? model of corrosion behaviour

Popis výsledku anglicky

This work is devoted to the study of changes of structure and chemical composition of two candidate materials for high-temperature power engineering. Materials are studied before and after their exposure to molten mixture 60 mol.% LiF + 40 mol.% NaF at temperature 953 K for exposure times 100, 300 and 1000 h. The exposition was carried out in a quasidynamic regime that simulated the flux of the coolant (the mixture of salts) in the pipeline. In Ni-alloy Ni-6 W-9 Mo-1.7 Ti-7 Cr (wt.%) severe corrosion damage was observed in the surface layer of thickness of about 100 ?m. In Ni-coated ferrite steel CSN 411523, elements redistribution close to the interface between the Ni layer/steel substrate was described by a simple model. The Ni layer showed excellentresistance against the corrosion, but its perforation and subsequent local damage of the substrate were also observed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

<a href="/cs/project/2A-1TP1%2F067" target="_blank" >2A-1TP1/067: Výzkum technologií pro přenos vysokopotencionálního tepla z jaderného zdroje.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

47

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—