Corrosion of chosen Ni-based material exposed to LiF-NaF molten salts

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354415" target="_blank" >RIV/68081723:_____/10:00354415 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Corrosion of chosen Ni-based material exposed to LiF-NaF molten salts
Popis výsledku v původním jazyce
This work is devoted to study of changes of structure and chemical composition in the surface layer of chosen candidate alloy Ni ? 6 W ? 9 Mo ? 1.7 Ti ? 7 Cr (in wt. %) for components of a LS-VHTR. The material was studied after its exposure to molten mixture 60 mol. % LiF + 40 mol. % NaF at temperature 993 and 1013K. The exposition was carried out in a quasidynamic regime, which simulates coolant (the mixture of salts) natural circulation conditions in components. The structure of the alloy was studiedby SEM. Severe corrosion damage was observed in the surface layer, which thickness was about 300 ?m.
Název v anglickém jazyce
Corrosion of chosen Ni-based material exposed to LiF-NaF molten salts
Popis výsledku anglicky
This work is devoted to study of changes of structure and chemical composition in the surface layer of chosen candidate alloy Ni ? 6 W ? 9 Mo ? 1.7 Ti ? 7 Cr (in wt. %) for components of a LS-VHTR. The material was studied after its exposure to molten mixture 60 mol. % LiF + 40 mol. % NaF at temperature 993 and 1013K. The exposition was carried out in a quasidynamic regime, which simulates coolant (the mixture of salts) natural circulation conditions in components. The structure of the alloy was studiedby SEM. Severe corrosion damage was observed in the surface layer, which thickness was about 300 ?m.

Projekt
<a href="/cs/project/2A-1TP1%2F067" target="_blank" >2A-1TP1/067: Výzkum technologií pro přenos vysokopotencionálního tepla z jaderného zdroje.</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku
Metal 2010. 19th International conference on metallurgy and materials - Conference Proceedings
ISBN
978-80-87294-17-8
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
—
Název nakladatele
Tanger s.r.o.
Místo vydání
Ostrava
Místo konání akce
Rožnov pod Radhoštěm
Datum konání akce
18. 5. 2010
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—

Podobné výsledky(10)