Two-Parameter Fracture Analysis of Wedge Splitting Test Specimens

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00332513" target="_blank" >RIV/68081723:_____/09:00332513 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Two-Parameter Fracture Analysis of Wedge Splitting Test Specimens

Popis výsledku v původním jazyce

The subject of the contribution is to gain new aspects of knowledge about the fracture behaviour of cementitious building materials by the wedge splitting test (WST). Particular attention is paid to the accurate description of the near crack-tip stress field in the WST specimen influenced particularly by the bottom boundary condition of the test inducing a vertical compressive force to the bottom part of the specimen in the area where the fracture is assumed to be propagating. To this aim a two-parameter constrained-based fracture mechanics is used. Different levels of constraint in the vicinity of the crack tip during fracture process through the specimen ligament are characterized by means of the T-stress. Attempts are made to consider even more thanthe two members of the Williams? series approximating the stress field in the cracked body. The problem is solved numerically by means of the finite element method and results are compared with data taken from the literature.

Název v anglickém jazyce

Two-Parameter Fracture Analysis of Wedge Splitting Test Specimens

Popis výsledku anglicky

The subject of the contribution is to gain new aspects of knowledge about the fracture behaviour of cementitious building materials by the wedge splitting test (WST). Particular attention is paid to the accurate description of the near crack-tip stress field in the WST specimen influenced particularly by the bottom boundary condition of the test inducing a vertical compressive force to the bottom part of the specimen in the area where the fracture is assumed to be propagating. To this aim a two-parameter constrained-based fracture mechanics is used. Different levels of constraint in the vicinity of the crack tip during fracture process through the specimen ligament are characterized by means of the T-stress. Attempts are made to consider even more thanthe two members of the Williams? series approximating the stress field in the cracked body. The problem is solved numerically by means of the finite element method and results are compared with data taken from the literature.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/KJB200410901" target="_blank" >KJB200410901: Lom silikátových kompozitů na vzorcích z jádrových vývrtů ? využití numerického modelování pro pokročilé stanovování lomových parametrů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the Twelfth International Conference on Civil, Structural and Enviromental Engineering Computing

ISBN

978-1-905088-31-7

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

—

Název nakladatele

Civil-Comp Press

Místo vydání

Stirlingshire

Místo konání akce

Funchal, Madeira

Datum konání akce

1. 9. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—