Influence of niobium alloying on the low cycle fatigue of cast TiAl alloys at room and high temperatures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00346327" target="_blank" >RIV/68081723:_____/10:00346327 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of niobium alloying on the low cycle fatigue of cast TiAl alloys at room and high temperatures

Popis výsledku v původním jazyce

The low-cycle fatigue properties of TiAl alloys with 2 at.% and 7 at.% of Nb with nearly lamellar microstructure were studied at room temperature and 750 degrees C. Cyclic hardening/softening curves, cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures as well as monotonic tensile properties. Both materials show stable cyclic response at 750 degrees C. At room temperature, significant cyclic hardening characteristic for 2 at.% Nb alloy is not observed for 7 at.%Nb alloy. This difference is attributed to higher Nb content which increases the stacking fault energy and thus prevents intensive twinning. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. The cyclic strength of the alloy with 7 at.% Nb is substantially higher in comparison with 2 at.% Nb, probably due to lower thickness of the lamellas.

Název v anglickém jazyce

Influence of niobium alloying on the low cycle fatigue of cast TiAl alloys at room and high temperatures

Popis výsledku anglicky

The low-cycle fatigue properties of TiAl alloys with 2 at.% and 7 at.% of Nb with nearly lamellar microstructure were studied at room temperature and 750 degrees C. Cyclic hardening/softening curves, cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures as well as monotonic tensile properties. Both materials show stable cyclic response at 750 degrees C. At room temperature, significant cyclic hardening characteristic for 2 at.% Nb alloy is not observed for 7 at.%Nb alloy. This difference is attributed to higher Nb content which increases the stacking fault energy and thus prevents intensive twinning. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. The cyclic strength of the alloy with 7 at.% Nb is substantially higher in comparison with 2 at.% Nb, probably due to lower thickness of the lamellas.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Procedia Engineering

ISSN

1877-7058

e-ISSN

—

Svazek periodika

2

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

9

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—