Fatigue life and fracture of cast gamma TiAl intermetallic alloy at room and elevated temperatures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00439947" target="_blank" >RIV/68081723:_____/11:00439947 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue life and fracture of cast gamma TiAl intermetallic alloy at room and elevated temperatures

Popis výsledku v původním jazyce

The low-cycle fatigue properties, surface relief and fracture surfaces of cast TiAl alloys with 2 at.% Nb having nearly lamellar microstructure were studied at room temperature and at 750 degrees C. Cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures. The surface relief and the fracture surfaces of fractured specimens were observed using scanning electron microscopy. At room temperature, significant cyclic hardening is observed whereas at 750 degrees C cyclic response was stable. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. Persistent slip markings formed along interlamellar interfaces were predominant locations for fatigue cracks at both temperatures. The cracks initiatedat surface or in sub-surface region led to the formation of smooth flat areas on the fracture surface corresponding to the persistent slip bands.

Název v anglickém jazyce

Fatigue life and fracture of cast gamma TiAl intermetallic alloy at room and elevated temperatures

Popis výsledku anglicky

The low-cycle fatigue properties, surface relief and fracture surfaces of cast TiAl alloys with 2 at.% Nb having nearly lamellar microstructure were studied at room temperature and at 750 degrees C. Cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures. The surface relief and the fracture surfaces of fractured specimens were observed using scanning electron microscopy. At room temperature, significant cyclic hardening is observed whereas at 750 degrees C cyclic response was stable. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. Persistent slip markings formed along interlamellar interfaces were predominant locations for fatigue cracks at both temperatures. The cracks initiatedat surface or in sub-surface region led to the formation of smooth flat areas on the fracture surface corresponding to the persistent slip bands.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F11%2F0704" target="_blank" >GAP107/11/0704: Optimalizace struktury a vlastnosti moderních vysokoteplotních litých materiálů legovaných uhlíkem pomocí komplexního tepelného zpracování</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2011 Conference Proceedings - Papers

ISBN

978-80-87294-24-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

969-974

Název nakladatele

Tanger s.r.o.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

18. 5. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—