High-cycle fatigue of Ni-base superalloy Inconel 713LC
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00353410" target="_blank" >RIV/68081723:_____/10:00353410 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
High-cycle fatigue of Ni-base superalloy Inconel 713LC
Popis výsledku v původním jazyce
Fatigue strength of three nominally identical batches of cast Ni-base superalloy INCONEL 713LC under load symmetrical cycling and cycling with tensile mean load was experimentally determined in high-cycle fatigue region at a temperature of 800 °C in air.Examination of fracture surfaces, crack initiation sites, microstructure and casting defects has been performed. Statistical method of largest extreme value distribution has been applied to characterize the casting defect distribution. The aim of the study was to evaluate the mean stress effect on high-cycle fatigue life, to explain the scatter of fatigue life data and a scatter related to material produced under nominally identical production conditions.
Název v anglickém jazyce
High-cycle fatigue of Ni-base superalloy Inconel 713LC
Popis výsledku anglicky
Fatigue strength of three nominally identical batches of cast Ni-base superalloy INCONEL 713LC under load symmetrical cycling and cycling with tensile mean load was experimentally determined in high-cycle fatigue region at a temperature of 800 °C in air.Examination of fracture surfaces, crack initiation sites, microstructure and casting defects has been performed. Statistical method of largest extreme value distribution has been applied to characterize the casting defect distribution. The aim of the study was to evaluate the mean stress effect on high-cycle fatigue life, to explain the scatter of fatigue life data and a scatter related to material produced under nominally identical production conditions.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
International Journal of Fatigue
ISSN
0142-1123
e-ISSN
—
Svazek periodika
32
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
6
Strana od-do
—
Kód UT WoS článku
000275890000007
EID výsledku v databázi Scopus
—