Initiation and propagation of fatigue cracks in cast IN713LC superalloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00353457" target="_blank" >RIV/68081723:_____/10:00353457 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Initiation and propagation of fatigue cracks in cast IN713LC superalloy
Popis výsledku v původním jazyce
Fatigue life, initiation and propagation of cracks at 800 °C in a cast Ni-base superalloy IN 713LC were experimentally studied in high-cycle fatigue region. Load symmetrical cycling and cycling with high tensile mean load were applied. Both crystallographic crack initiation resulting in long Stage I crack growth and non-crystallographic Stage II propagation were observed. High scatter of fatigue life data was explained by (i) variability in microstructural conditions for crystallographic crack initiation and propagation and by (ii) influence of casting defect size distribution. The fractographic observation supports the slip band decohesion mechanism of crack initiation and an important role of cyclic slip localization in persistent slip bands.
Název v anglickém jazyce
Initiation and propagation of fatigue cracks in cast IN713LC superalloy
Popis výsledku anglicky
Fatigue life, initiation and propagation of cracks at 800 °C in a cast Ni-base superalloy IN 713LC were experimentally studied in high-cycle fatigue region. Load symmetrical cycling and cycling with high tensile mean load were applied. Both crystallographic crack initiation resulting in long Stage I crack growth and non-crystallographic Stage II propagation were observed. High scatter of fatigue life data was explained by (i) variability in microstructural conditions for crystallographic crack initiation and propagation and by (ii) influence of casting defect size distribution. The fractographic observation supports the slip band decohesion mechanism of crack initiation and an important role of cyclic slip localization in persistent slip bands.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Engineering Fracture Mechanics
ISSN
0013-7944
e-ISSN
—
Svazek periodika
77
Číslo periodika v rámci svazku
11
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
—
Kód UT WoS článku
000280285800034
EID výsledku v databázi Scopus
—