Modelling of degradation processes in creep resistant steels through accelerated creep tests after long-term isothermal ageing

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00367195" target="_blank" >RIV/68081723:_____/10:00367195 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Modelling of degradation processes in creep resistant steels through accelerated creep tests after long-term isothermal ageing
Popis výsledku v původním jazyce
The accelerated high temperature creep tests were performed on P91, P92 and P23 steels in an effort to obtain a more complete description of the role of microstructural stability of these steels.It has been found that under restricted oxidation due to argon atmosphere microstructural instability is the main detrimental process in the long-term degradation of the creep rupture strength of these steels.
Název v anglickém jazyce
Modelling of degradation processes in creep resistant steels through accelerated creep tests after long-term isothermal ageing
Popis výsledku anglicky
The accelerated high temperature creep tests were performed on P91, P92 and P23 steels in an effort to obtain a more complete description of the role of microstructural stability of these steels.It has been found that under restricted oxidation due to argon atmosphere microstructural instability is the main detrimental process in the long-term degradation of the creep rupture strength of these steels.

Projekt
<a href="/cs/project/2A-1TP1%2F057" target="_blank" >2A-1TP1/057: Řešení materiálových a technologických inovací pro energetická a chemická zařízení nové generace pracující za vysokých teplot.</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)