METALLURGY AND PROPERTIES OF ADVANCED NiAl-Mo EUTECTICS

Popis výsledku v původním jazyce

A NiAl-Mo eutectic alloy was melt from 99,99% purity components and cast by the drop casting technique. The drop-cast ternary alloy (nominal composition of Ni-45Al-9Mo at. %), was re-melted and directionally solidified using a high temperature optical floating zone furnace. A resulting in-situ composite consists of Ni-45,2Al matrix and Mo-10Al-4Ni fibers, all in at. %. The volume fraction of 14% Mo-fibers stems from the eutectic composition. Backscatter diffraction shows that the NiAl-matrix and the Mo-fibers are both < 001 >-oriented with respect to the axis of the cylindrical rods. Preliminary creep experiments confirmed an immense improvement of high temperature strength due to the fine distribution of Mo-fibres. The amount of strengthening in termsof minimum creep rate can be as high as 7 orders of magnitude. Post-mortem transmission electron microscopy experiments provided evidence that creep in the temperature range of 800 - 900 degrees C results in an extensive formation of sub

Název v anglickém jazyce

METALLURGY AND PROPERTIES OF ADVANCED NiAl-Mo EUTECTICS

Popis výsledku anglicky

A NiAl-Mo eutectic alloy was melt from 99,99% purity components and cast by the drop casting technique. The drop-cast ternary alloy (nominal composition of Ni-45Al-9Mo at. %), was re-melted and directionally solidified using a high temperature optical floating zone furnace. A resulting in-situ composite consists of Ni-45,2Al matrix and Mo-10Al-4Ni fibers, all in at. %. The volume fraction of 14% Mo-fibers stems from the eutectic composition. Backscatter diffraction shows that the NiAl-matrix and the Mo-fibers are both < 001 >-oriented with respect to the axis of the cylindrical rods. Preliminary creep experiments confirmed an immense improvement of high temperature strength due to the fine distribution of Mo-fibres. The amount of strengthening in termsof minimum creep rate can be as high as 7 orders of magnitude. Post-mortem transmission electron microscopy experiments provided evidence that creep in the temperature range of 800 - 900 degrees C results in an extensive formation of sub

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA202%2F09%2F2073" target="_blank" >GA202/09/2073: Deformační mechanismy in-situ kompozitních materiálů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2010: 19TH INTERNATIONAL METALLURGICAL AND MATERIALS CONFERENCE

ISBN

978-80-87294-17-8

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

888-891

Název nakladatele

TANGER LTD

Místo vydání

Ostrava

Místo konání akce

Rožnov pod Radhoštěm

Datum konání akce

18. 5. 2010

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000286658700154