Fatigue cracks in Eurofer 97 steel: Part I. Nucleation and small crack growth kinetics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00359062" target="_blank" >RIV/68081723:_____/11:00359062 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jnucmat.2011.01.010" target="_blank" >http://dx.doi.org/10.1016/j.jnucmat.2011.01.010</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jnucmat.2011.01.010" target="_blank" >10.1016/j.jnucmat.2011.01.010</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue cracks in Eurofer 97 steel: Part I. Nucleation and small crack growth kinetics

Popis výsledku v původním jazyce

Fatigue crack nucleation and growth were studied in the Eurofer 97 ferritic?martensitic steel at room temperature. Cylindrical specimens with a shallow notch and no artificial crack starters were used. The constant strain amplitude cycling was adopted. First fatigue cracks nucleate at about 5% of the fatigue life along the surface slip bands. If a crack overcome the barrier of the first high angle boundary, its growth is regular and an exponential growth law is observed. This law may be used for the residual fatigue life prediction based on the small crack growth kinetics.

Název v anglickém jazyce

Fatigue cracks in Eurofer 97 steel: Part I. Nucleation and small crack growth kinetics

Popis výsledku anglicky

Fatigue crack nucleation and growth were studied in the Eurofer 97 ferritic?martensitic steel at room temperature. Cylindrical specimens with a shallow notch and no artificial crack starters were used. The constant strain amplitude cycling was adopted. First fatigue cracks nucleate at about 5% of the fatigue life along the surface slip bands. If a crack overcome the barrier of the first high angle boundary, its growth is regular and an exponential growth law is observed. This law may be used for the residual fatigue life prediction based on the small crack growth kinetics.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Nuclear Materials

ISSN

0022-3115

e-ISSN

—

Svazek periodika

412

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

2-6

Kód UT WoS článku

000291171400001

EID výsledku v databázi Scopus

—