Microstructural stability of ultrafine grained copper at elevated temperature

Kód výsledku v IS VaVaI

RIV/68081723:_____/11:00366907 - isvavai.cz

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructural stability of ultrafine grained copper at elevated temperature

Popis výsledku v původním jazyce

Thermal stability of ultrafine grained (UFG) structure of 99.9% pure copper produced by eight equal channel angular pressing (ECAP) passes was studied. The annealing experiments were conducted at temperature range from 180 °C to 300 °C in a tube furnaceunder argon as a protecting gas. The dwell times were in the range from 10 min to 300 min. The electron backscattering diffraction (EBSD) analyses were performed before and after annealing at exactly the same area in order to quantify the changes of UFGstructure. More advanced analysis of the EBSD results based on kernel average misorientation (KAM) parameter was performed.

Název v anglickém jazyce

Microstructural stability of ultrafine grained copper at elevated temperature

Popis výsledku anglicky

Thermal stability of ultrafine grained (UFG) structure of 99.9% pure copper produced by eight equal channel angular pressing (ECAP) passes was studied. The annealing experiments were conducted at temperature range from 180 °C to 300 °C in a tube furnaceunder argon as a protecting gas. The dwell times were in the range from 10 min to 300 min. The electron backscattering diffraction (EBSD) analyses were performed before and after annealing at exactly the same area in order to quantify the changes of UFGstructure. More advanced analysis of the EBSD results based on kernel average misorientation (KAM) parameter was performed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1338-1156

e-ISSN

—

Svazek periodika

17

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

5

Strana od-do

158-162

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—