Fatigue crack growth and delamination in fiber metal laminate (GLARE) during loading with positive mean stress
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00377731" target="_blank" >RIV/68081723:_____/12:00377731 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue crack growth and delamination in fiber metal laminate (GLARE) during loading with positive mean stress
Popis výsledku v původním jazyce
The aim of the paper is to present the results of a study on the damage of fiber metal laminate (GLARE) subjected to the low cycle fatigue loading with positive mean stress. The fatigue crack initiation and growth was observed on the surface of notched specimens and then the individual layers of fatigued specimens were removed by chemical etching and polishing to obtain data about cracks length and delamination shape and area. Mechanism of initiation and crack growth in this type of materials differs from homogeneous monolithic materials. The fatigue life in term of number of cycles to crack initiation depending on amplitude of local plastic deformation and local stress in the notch root was evaluated.
Název v anglickém jazyce
Fatigue crack growth and delamination in fiber metal laminate (GLARE) during loading with positive mean stress
Popis výsledku anglicky
The aim of the paper is to present the results of a study on the damage of fiber metal laminate (GLARE) subjected to the low cycle fatigue loading with positive mean stress. The fatigue crack initiation and growth was observed on the surface of notched specimens and then the individual layers of fatigued specimens were removed by chemical etching and polishing to obtain data about cracks length and delamination shape and area. Mechanism of initiation and crack growth in this type of materials differs from homogeneous monolithic materials. The fatigue life in term of number of cycles to crack initiation depending on amplitude of local plastic deformation and local stress in the notch root was evaluated.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F09%2F1954" target="_blank" >GA106/09/1954: Role oxidické disperze při únavovém chování ODS ocelí</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of Engineering Mechanics 2012
ISBN
978-80-86246-40-6
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
531-536
Název nakladatele
Institute of Theoretical and Applied Mechanics AS CR, v.v.i
Místo vydání
Praha
Místo konání akce
Svratka
Datum konání akce
14. 5. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—