Fatigue Crack Paths in Cast Inconel 713LC with/without Al Diffusion Coating under Various Loading and Temperature Conditions
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00399682" target="_blank" >RIV/68081723:_____/12:00399682 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/12:PU102503
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue Crack Paths in Cast Inconel 713LC with/without Al Diffusion Coating under Various Loading and Temperature Conditions
Popis výsledku v původním jazyce
Fatigue crack paths in cast Inconel 713LC with and without Al diffusion coating were studied under various loading and temperature conditions. Both coated and uncoated specimens were fatigued under symmetric bending, symmetric torsion and in-phase bending-torsion loading at room temperature and under a fully reversed push-pull straining at 800 °C. Optical and scanning electron microscopy were used to study fracture surfaces and polished sections of the gauge segments cut parallel to the specimen axis. The image analysis software was employed to determine the percentage of carbides on both the fracture surfaces and etched specimen sections.
Název v anglickém jazyce
Fatigue Crack Paths in Cast Inconel 713LC with/without Al Diffusion Coating under Various Loading and Temperature Conditions
Popis výsledku anglicky
Fatigue crack paths in cast Inconel 713LC with and without Al diffusion coating were studied under various loading and temperature conditions. Both coated and uncoated specimens were fatigued under symmetric bending, symmetric torsion and in-phase bending-torsion loading at room temperature and under a fully reversed push-pull straining at 800 °C. Optical and scanning electron microscopy were used to study fracture surfaces and polished sections of the gauge segments cut parallel to the specimen axis. The image analysis software was employed to determine the percentage of carbides on both the fracture surfaces and etched specimen sections.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the 4th International Conference on Crack Paths (CP 2012)
ISBN
9788895940441
ISSN
2281-1060
e-ISSN
—
Počet stran výsledku
8
Strana od-do
967-974
Název nakladatele
University of Parma
Místo vydání
Parma
Místo konání akce
Gaeta
Datum konání akce
19. 9. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—