Experimental study on the origin of crack initiation in fatigued metals

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00399547" target="_blank" >RIV/68081723:_____/13:00399547 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Experimental study on the origin of crack initiation in fatigued metals

Popis výsledku v původním jazyce

Early stages of surface relief evolution of persistent slip markings (PSMs) were studied by atomic force microscopy (AFM) and high-resolution scanning electron microscopy (SEM? FEG) on two polycrystalline materials ? 316L austenitic stainless steel fatigued at 93 K, 173 K and 573 K and copper fatigued at 83 K, 173 K and 295 K. Experimental data on the morphology of PSMs, occurrence of extrusions and intrusions and the kinetics of extrusion growth are discussed with respect to the formation of point defects within areas of localized cyclic slip (persistent slip bands ? PSBs) and especially to their mobility at different temperatures. The importance of mass redistribution due to the migration of respective type of point defects for PSM formation and creation of fatigue crack embryos, i.e. sharp intrusions is highlighted.

Název v anglickém jazyce

Experimental study on the origin of crack initiation in fatigued metals

Popis výsledku anglicky

Early stages of surface relief evolution of persistent slip markings (PSMs) were studied by atomic force microscopy (AFM) and high-resolution scanning electron microscopy (SEM? FEG) on two polycrystalline materials ? 316L austenitic stainless steel fatigued at 93 K, 173 K and 573 K and copper fatigued at 83 K, 173 K and 295 K. Experimental data on the morphology of PSMs, occurrence of extrusions and intrusions and the kinetics of extrusion growth are discussed with respect to the formation of point defects within areas of localized cyclic slip (persistent slip bands ? PSBs) and especially to their mobility at different temperatures. The importance of mass redistribution due to the migration of respective type of point defects for PSM formation and creation of fatigue crack embryos, i.e. sharp intrusions is highlighted.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F2371" target="_blank" >GAP108/10/2371: Lokalizace a ireverzibilita cyklického skluzu v polykrystalech</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the Seventh International Conference on Low Cycle Fatigue - LCF7

ISBN

978-3-9814516-2-7

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

391-396

Název nakladatele

DMV

Místo vydání

Berlín

Místo konání akce

Aachen

Datum konání akce

9. 9. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—