AFM and SEM-FEG study on fundamental mechanisms leading to fatigue crack initiation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00453925" target="_blank" >RIV/68081723:_____/15:00453925 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00177016:_____/15:#0001228

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.ijfatigue.2014.09.019" target="_blank" >http://dx.doi.org/10.1016/j.ijfatigue.2014.09.019</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ijfatigue.2014.09.019" target="_blank" >10.1016/j.ijfatigue.2014.09.019</a>

Jazyk výsledku

angličtina

Název v původním jazyce

AFM and SEM-FEG study on fundamental mechanisms leading to fatigue crack initiation

Popis výsledku v původním jazyce

Early stages of surface relief evolution of persistent slip markings (PSMs) in polycrystalline 316L austenitic stainless steel cycled with constant plastic strain amplitude at 93, 173 and 573 K were studied using atomic force microscopy (AFM) and high-resolution scanning electron microscopy (SEM-FEG). Qualitative and quantitative data on the morphology of PSMs, occurrence of extrusions and intrusions and the kinetics of extrusion growth are reported for all temperatures. PSMs start in all cases as surface extrusions which are later accompanied by formation of intrusions. This finding is discussed with respect to the point defect formation within areas of localized cyclic slip and primarily to their mobility at different temperatures. Consequences of migration of respective point defects for surface relief formation and the conditions for creation of fatigue crack embryos, i.e. sharp intrusions are highlighted.

Název v anglickém jazyce

AFM and SEM-FEG study on fundamental mechanisms leading to fatigue crack initiation

Popis výsledku anglicky

Early stages of surface relief evolution of persistent slip markings (PSMs) in polycrystalline 316L austenitic stainless steel cycled with constant plastic strain amplitude at 93, 173 and 573 K were studied using atomic force microscopy (AFM) and high-resolution scanning electron microscopy (SEM-FEG). Qualitative and quantitative data on the morphology of PSMs, occurrence of extrusions and intrusions and the kinetics of extrusion growth are reported for all temperatures. PSMs start in all cases as surface extrusions which are later accompanied by formation of intrusions. This finding is discussed with respect to the point defect formation within areas of localized cyclic slip and primarily to their mobility at different temperatures. Consequences of migration of respective point defects for surface relief formation and the conditions for creation of fatigue crack embryos, i.e. sharp intrusions are highlighted.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Fatigue

ISSN

0142-1123

e-ISSN

—

Svazek periodika

76

Číslo periodika v rámci svazku

JUL

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

11-18

Kód UT WoS článku

000353177900002

EID výsledku v databázi Scopus

2-s2.0-84939943069