LCF behaviour of ultrafine grained 301LN stainless steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00433871" target="_blank" >RIV/68081723:_____/14:00433871 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.proeng.2014.06.239" target="_blank" >http://dx.doi.org/10.1016/j.proeng.2014.06.239</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.proeng.2014.06.239" target="_blank" >10.1016/j.proeng.2014.06.239</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
LCF behaviour of ultrafine grained 301LN stainless steel
Popis výsledku v původním jazyce
Cyclic strain behaviour of metastable austenitic 301LN steel with different grain sizes ? coarse (14 ?m) and ultrafine (1.4 ?m) grained ? produced by the special thermo-mechanical treatment based on the martensite-to-austenite reversion was investigated.Low-cycle fatigue (LCF) tests were conducted on flat specimens at room temperature in fully push-pull mode under strain control with constant strain rate of 210?3 s?1 and constant total strain amplitude ranging from 0.4% to 0.9%. LCF behaviour was characterised by cyclic hardening/softening curves and fatigue life curves. After completion of fatigue tests surface fatigue damage was studied using scanning electron microscopy (SEM). Ferritoscope was adopted to reveal the destabilization of austenitic structure and evaluate the extent of deformation induced martensitic transformation.
Název v anglickém jazyce
LCF behaviour of ultrafine grained 301LN stainless steel
Popis výsledku anglicky
Cyclic strain behaviour of metastable austenitic 301LN steel with different grain sizes ? coarse (14 ?m) and ultrafine (1.4 ?m) grained ? produced by the special thermo-mechanical treatment based on the martensite-to-austenite reversion was investigated.Low-cycle fatigue (LCF) tests were conducted on flat specimens at room temperature in fully push-pull mode under strain control with constant strain rate of 210?3 s?1 and constant total strain amplitude ranging from 0.4% to 0.9%. LCF behaviour was characterised by cyclic hardening/softening curves and fatigue life curves. After completion of fatigue tests surface fatigue damage was studied using scanning electron microscopy (SEM). Ferritoscope was adopted to reveal the destabilization of austenitic structure and evaluate the extent of deformation induced martensitic transformation.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
XVII International Colloquium on Mechanical Fatigue of Metals (ICMFM17)
ISBN
—
ISSN
1877-7058
e-ISSN
—
Počet stran výsledku
4
Strana od-do
147-150
Název nakladatele
Elsevier
Místo vydání
Amsterdam
Místo konání akce
Verbania
Datum konání akce
25. 6. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—