LCF behaviour of 301LN steel: coarse-grained vs. UFG-bimodal structure

Popis výsledku v původním jazyce

Low-cycle fatigue (LCF) behaviour of metastable austenitic 301LN steel with different grain sizes – coarse-grained (14 µm) and UFG (1.4 µm) with a grain bimodality – produced by reversion annealing (RA) was investigated. Symmetrical push-pull LCF tests were conducted on flat sheet specimens at room temperature with constant strain rate of 2×10–3 s–1 and constant total strain amplitude ranging from 0.4% to 0.8%. After completion of fatigue tests a ferritescope was adopted for quantitative assessment of volume fraction of deformation induced martensite (DIM). Microstructural changes, distribution and morphology of DIM in the volume of material were characterized at different scales by colour etching, TEM and EBSD techniques. Experimental data on microstructural changes are confronted with the stress-strain response and with the chemical heterogeneity present in the material.

Název v anglickém jazyce

LCF behaviour of 301LN steel: coarse-grained vs. UFG-bimodal structure

Popis výsledku anglicky

Low-cycle fatigue (LCF) behaviour of metastable austenitic 301LN steel with different grain sizes – coarse-grained (14 µm) and UFG (1.4 µm) with a grain bimodality – produced by reversion annealing (RA) was investigated. Symmetrical push-pull LCF tests were conducted on flat sheet specimens at room temperature with constant strain rate of 2×10–3 s–1 and constant total strain amplitude ranging from 0.4% to 0.8%. After completion of fatigue tests a ferritescope was adopted for quantitative assessment of volume fraction of deformation induced martensite (DIM). Microstructural changes, distribution and morphology of DIM in the volume of material were characterized at different scales by colour etching, TEM and EBSD techniques. Experimental data on microstructural changes are confronted with the stress-strain response and with the chemical heterogeneity present in the material.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

<a href="/cs/project/GA13-32665S" target="_blank" >GA13-32665S: Mechanismy únavového poškozování u ultrajemnozrnných nerezavějících ocelí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

LCF8 Eighth International Conference on Low Cycle Fatigue

ISBN

978-3-9814516-5-8

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

205-210

Název nakladatele

DVM e.V.

Místo vydání

Berlin

Místo konání akce

Dresden

Datum konání akce

27. 6. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—