Thermo-mechanical and isothermal fatigue behavior of austenitic stainless steel AISI 316L

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00449806" target="_blank" >RIV/68081723:_____/15:00449806 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/15:PU119276

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Thermo-mechanical and isothermal fatigue behavior of austenitic stainless steel AISI 316L

Popis výsledku v původním jazyce

Many structural components of nuclear power plant systems are made of austenitic stainless steels. These structures undergo degradation by thermo-mechanical fatigue (TMF) caused by simultaneous cyclic straining and temperature cycling, particularly during start-up, shut-down and transient operations. The present work reports the cyclic deformation behavior and fatigue damage of austenitic stainless steel AISI 316L during TMF and isothermal fatigue (IF) testing in air. Total strain controlled in-phase TMF loading in the temperature range 200 - 600 °C and isothermal fatigue (IF) at 600 °C were performed. Hardening/softening curves, cyclic stress-strain response and fatigue life diagrams were obtained both for TMF and IF tests. Fatigue damage was documented using surface relief and fracture surface observations. Mean stress evolution and fatigue degradation data are employed to discuss the fatigue behavior of 316L steel both in TMF and IF regimes.

Název v anglickém jazyce

Thermo-mechanical and isothermal fatigue behavior of austenitic stainless steel AISI 316L

Popis výsledku anglicky

Many structural components of nuclear power plant systems are made of austenitic stainless steels. These structures undergo degradation by thermo-mechanical fatigue (TMF) caused by simultaneous cyclic straining and temperature cycling, particularly during start-up, shut-down and transient operations. The present work reports the cyclic deformation behavior and fatigue damage of austenitic stainless steel AISI 316L during TMF and isothermal fatigue (IF) testing in air. Total strain controlled in-phase TMF loading in the temperature range 200 - 600 °C and isothermal fatigue (IF) at 600 °C were performed. Hardening/softening curves, cyclic stress-strain response and fatigue life diagrams were obtained both for TMF and IF tests. Fatigue damage was documented using surface relief and fracture surface observations. Mean stress evolution and fatigue degradation data are employed to discuss the fatigue behavior of 316L steel both in TMF and IF regimes.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metal 2015: 24th International Conference on Metallurgy and Materials

ISBN

978-80-87294-58-1

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

TANGER Ltd

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

3. 6. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—