Fracture and Damage Behavior in an Advanced Heat Resistant Austenitic Stainless Steel During LCF, TMF and CF
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00500115" target="_blank" >RIV/68081723:_____/18:00500115 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.prostr.2018.12.161" target="_blank" >http://dx.doi.org/10.1016/j.prostr.2018.12.161</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.prostr.2018.12.161" target="_blank" >10.1016/j.prostr.2018.12.161</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fracture and Damage Behavior in an Advanced Heat Resistant Austenitic Stainless Steel During LCF, TMF and CF
Popis výsledku v původním jazyce
Future advanced ultra-supercritical power plant will be run at higher temperature and pressure. New materials will be used to meet the requirements. However, the structure integrity of these materials needs to be evaluated. Sanicro 25 is a newly developed advanced austenitic heat resistant stainless steel with the aim to be used in future 700 degrees C or 650 degrees C power plants to replace part of Ni based alloys. This paper provides an overview on the fracture and damage behavior in this material during LCF, TMF and CF. The cyclic hardening and fatigue life during LCF, TMF and CF will be discussed. The influence of prolonged service degradation has been analyzed by the use of pre-aged material for TMF and CF loading conditions
Název v anglickém jazyce
Fracture and Damage Behavior in an Advanced Heat Resistant Austenitic Stainless Steel During LCF, TMF and CF
Popis výsledku anglicky
Future advanced ultra-supercritical power plant will be run at higher temperature and pressure. New materials will be used to meet the requirements. However, the structure integrity of these materials needs to be evaluated. Sanicro 25 is a newly developed advanced austenitic heat resistant stainless steel with the aim to be used in future 700 degrees C or 650 degrees C power plants to replace part of Ni based alloys. This paper provides an overview on the fracture and damage behavior in this material during LCF, TMF and CF. The cyclic hardening and fatigue life during LCF, TMF and CF will be discussed. The influence of prolonged service degradation has been analyzed by the use of pre-aged material for TMF and CF loading conditions
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
ECF22 - Loading and Environmental effects on Structural Integrity
ISBN
—
ISSN
2452-3216
e-ISSN
—
Počet stran výsledku
6
Strana od-do
843-848
Název nakladatele
Elsevier
Místo vydání
Amsterdam
Místo konání akce
Belgrade
Datum konání akce
26. 8. 2018
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000459860900138