The application of miniaturized three-point-bend specimens for determination of the reference temperature of JRQ steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00450454" target="_blank" >RIV/68081723:_____/15:00450454 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1115/PVP2015-45706" target="_blank" >http://dx.doi.org/10.1115/PVP2015-45706</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1115/PVP2015-45706" target="_blank" >10.1115/PVP2015-45706</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The application of miniaturized three-point-bend specimens for determination of the reference temperature of JRQ steel
Popis výsledku v původním jazyce
This contribution deals with determination of the reference temperature of JRQ steel using miniaturized specimens. The dimensions of used miniaturized specimens were 3 4 27 mm (thickness width length). This specimen type offers the utilization of limitedamount of test material or broken halves of precracked Charpy and larger specimens. The test material comes from the broken halves of 0.5T SEB specimens previously tested for purposes of the reference temperature determination in Ciemat, Madrid. The fracture toughness tests of specimens were performed in the transition region of the steel according to the recommendations of standard ASTM E1921 and according Wallin?s recommended temperature range for miniaturized specimens. The determined reference temperature of the Master Curve was very similar to the determined ones from three point bend specimen of sizes 0.2T, 0.4T and 0.5T. The obtained results confirm a necessity of conduct of tests at low temperatures and testing sufficient numbe
Název v anglickém jazyce
The application of miniaturized three-point-bend specimens for determination of the reference temperature of JRQ steel
Popis výsledku anglicky
This contribution deals with determination of the reference temperature of JRQ steel using miniaturized specimens. The dimensions of used miniaturized specimens were 3 4 27 mm (thickness width length). This specimen type offers the utilization of limitedamount of test material or broken halves of precracked Charpy and larger specimens. The test material comes from the broken halves of 0.5T SEB specimens previously tested for purposes of the reference temperature determination in Ciemat, Madrid. The fracture toughness tests of specimens were performed in the transition region of the steel according to the recommendations of standard ASTM E1921 and according Wallin?s recommended temperature range for miniaturized specimens. The determined reference temperature of the Master Curve was very similar to the determined ones from three point bend specimen of sizes 0.2T, 0.4T and 0.5T. The obtained results confirm a necessity of conduct of tests at low temperatures and testing sufficient numbe
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the ASME 2015 Pressure Vessels & Piping Conference PVP2015
ISBN
978-0-7918-5693-2
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1-6
Název nakladatele
ASME
Místo vydání
Boston
Místo konání akce
Boston
Datum konání akce
19. 7. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—