THE EFFECT OF SPECIMEN SIZE FOR THE P91 STEEL AT ELEVATED AND HIGH TEMPERATURES
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00511063" target="_blank" >RIV/68081723:_____/17:00511063 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
THE EFFECT OF SPECIMEN SIZE FOR THE P91 STEEL AT ELEVATED AND HIGH TEMPERATURES
Popis výsledku v původním jazyce
The contribution aims to evaluate fracture toughness of the P91 steel in the ductile regime. This steel is broadly used for applications for pressure vessels and piping systems. The J-R curves were obtained using 1T, 0.5T and 0.25T CT specimens at 23 degrees C and using 0.5T and 0.25T CT specimens up to 600 degrees C. The energy normalization method for the J-R curve determination according to the ASTM E1820 was used. The resistance to crack propagation shows temperature dependence and the dynamic strain ageing effect with minimum values at 400 degrees C. Both specimen sizes 0.5T and 0.25T give a similar trend of the temperature dependence of fracture toughness. However, the size effect is observed as fracture toughness decreases with the specimen size. The results obtained are compared with the results of other authors pointing the specimen size effect and the temperature dependence of the steel.
Název v anglickém jazyce
THE EFFECT OF SPECIMEN SIZE FOR THE P91 STEEL AT ELEVATED AND HIGH TEMPERATURES
Popis výsledku anglicky
The contribution aims to evaluate fracture toughness of the P91 steel in the ductile regime. This steel is broadly used for applications for pressure vessels and piping systems. The J-R curves were obtained using 1T, 0.5T and 0.25T CT specimens at 23 degrees C and using 0.5T and 0.25T CT specimens up to 600 degrees C. The energy normalization method for the J-R curve determination according to the ASTM E1820 was used. The resistance to crack propagation shows temperature dependence and the dynamic strain ageing effect with minimum values at 400 degrees C. Both specimen sizes 0.5T and 0.25T give a similar trend of the temperature dependence of fracture toughness. However, the size effect is observed as fracture toughness decreases with the specimen size. The results obtained are compared with the results of other authors pointing the specimen size effect and the temperature dependence of the steel.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, 2017, VOL 1A
ISBN
978-0-7918-5790-8
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
V01AT01A068
Název nakladatele
ASME
Místo vydání
New York
Místo konání akce
Waikoloa, Hawaii
Datum konání akce
16. 7. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000422810300068