The prediction of size effect on J R curve for Eurofer97 steel by simplified mechanical model
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00450456" target="_blank" >RIV/68081723:_____/15:00450456 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1115/PVP2015-45703" target="_blank" >http://dx.doi.org/10.1115/PVP2015-45703</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1115/PVP2015-45703" target="_blank" >10.1115/PVP2015-45703</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The prediction of size effect on J R curve for Eurofer97 steel by simplified mechanical model
Popis výsledku v původním jazyce
The possibilities to derive fracture toughness from small specimens are naturally limited due to constraint requirements which are especially restrictive in toughness testing. The loss of constraint at the crack tip is more likely to occur as specimen size decreases. Application of miniature specimens in fracture toughness testing thus requires a suitable methodology or correction procedure to deal with phenomenon of the constraint loss. Schindler et al. have proposed a simplified mechanical model thatcan be used to scale up the key test characteristics from miniature specimen to the larger one. The model is applied to the miniature bending specimens to describe size effect on J R curve of the Eurofer97 steel. The examined steel exhibits quite high toughness values at upper shelf region of fracture toughness. As a result, experimentally determined J R curves of three different sizes of pre cracked bending specimens showed high values of J integral, which were significantly different e
Název v anglickém jazyce
The prediction of size effect on J R curve for Eurofer97 steel by simplified mechanical model
Popis výsledku anglicky
The possibilities to derive fracture toughness from small specimens are naturally limited due to constraint requirements which are especially restrictive in toughness testing. The loss of constraint at the crack tip is more likely to occur as specimen size decreases. Application of miniature specimens in fracture toughness testing thus requires a suitable methodology or correction procedure to deal with phenomenon of the constraint loss. Schindler et al. have proposed a simplified mechanical model thatcan be used to scale up the key test characteristics from miniature specimen to the larger one. The model is applied to the miniature bending specimens to describe size effect on J R curve of the Eurofer97 steel. The examined steel exhibits quite high toughness values at upper shelf region of fracture toughness. As a result, experimentally determined J R curves of three different sizes of pre cracked bending specimens showed high values of J integral, which were significantly different e
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
ASME 2015 Pressure Vessels and Piping Conference
ISBN
978-0-7918-5692-5
ISSN
—
e-ISSN
—
Počet stran výsledku
9
Strana od-do
1-9
Název nakladatele
ASME
Místo vydání
Boston
Místo konání akce
Boston
Datum konání akce
19. 7. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—