Creep Damage and Fracture in Advanced Tungsten Modified 9%Cr Ferritic Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00463822" target="_blank" >RIV/68081723:_____/16:00463822 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.713.183" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.713.183</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.713.183" target="_blank" >10.4028/www.scientific.net/KEM.713.183</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Creep Damage and Fracture in Advanced Tungsten Modified 9%Cr Ferritic Steel

Popis výsledku v původním jazyce

Advanced tungsten modified 9%Cr ferritic steel (ASTM Grade P92) is a promising material for the next generation of fossil and nuclear power plants. Unfortunately, there are rather few published reports on damage processes in P92 steel during high temperature creep and the effect of damage evolution on the creep strength is not fully understood. In this work, the creep behaviour of P92 steel in as-received condition and after long-term isothermal ageing was investigated at 600 and 650°C using uniaxial tension creep tests. To quantify the effect of each damage process on the loss of creep strength, most of creep tests were followed by microstructural and fractographic investigations. It was found that the large Laves phase particles, which coarsened during creep exposure, served as preferential sites for creep cavity nucleation.

Název v anglickém jazyce

Creep Damage and Fracture in Advanced Tungsten Modified 9%Cr Ferritic Steel

Popis výsledku anglicky

Advanced tungsten modified 9%Cr ferritic steel (ASTM Grade P92) is a promising material for the next generation of fossil and nuclear power plants. Unfortunately, there are rather few published reports on damage processes in P92 steel during high temperature creep and the effect of damage evolution on the creep strength is not fully understood. In this work, the creep behaviour of P92 steel in as-received condition and after long-term isothermal ageing was investigated at 600 and 650°C using uniaxial tension creep tests. To quantify the effect of each damage process on the loss of creep strength, most of creep tests were followed by microstructural and fractographic investigations. It was found that the large Laves phase particles, which coarsened during creep exposure, served as preferential sites for creep cavity nucleation.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA16-09518S" target="_blank" >GA16-09518S: Mechanismy creepového porušování pokročilé 9%Cr feritické oceli modifikované wolframem</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Advances in Fracture and Damage Mechanics XV

ISBN

978-3-03835-716-2

ISSN

1013-9826

e-ISSN

—

Počet stran výsledku

4

Strana od-do

183-186

Název nakladatele

Trans Tech Publications Ltd

Místo vydání

Pfaffikon

Místo konání akce

Alicante

Datum konání akce

14. 9. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—