Description of short fatigue crack propagation under low cycle fatigue regime

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00465128" target="_blank" >RIV/68081723:_____/16:00465128 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.prostr.2016.06.377" target="_blank" >http://dx.doi.org/10.1016/j.prostr.2016.06.377</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.prostr.2016.06.377" target="_blank" >10.1016/j.prostr.2016.06.377</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Description of short fatigue crack propagation under low cycle fatigue regime

Popis výsledku v původním jazyce

Measurement of the short fatigue crack propagation can come across a lot of difficulties from the experimental point of view and interpretation of the results is also sometimes controversial. For simplicity, usual description of the short cracks is based on linear elastic fracture mechanics (using the concept of stress intensity factor). In this case, significant differences between short cracks and long cracks are usually presented. Most of the discrepancies are simply given by non-validity of the linear elastic fracture mechanics approach. In our case of physically short fatigue cracks the level of applied stress is close to cyclic yield stress of the material and, due to large amount of plasticity, conditions of linear elastic fracture mechanics are not satisfied. As a consequence, non-linear elastic plastic fracture mechanics is used for description of the short crack behavior in this article. Concept based on plastic part of J-integral is proposed for the description of the short crack behavior and data obtained for different strain amplitudes are compared. This concept is validated on experimental data obtained on steel 316L.

Název v anglickém jazyce

Description of short fatigue crack propagation under low cycle fatigue regime

Popis výsledku anglicky

Measurement of the short fatigue crack propagation can come across a lot of difficulties from the experimental point of view and interpretation of the results is also sometimes controversial. For simplicity, usual description of the short cracks is based on linear elastic fracture mechanics (using the concept of stress intensity factor). In this case, significant differences between short cracks and long cracks are usually presented. Most of the discrepancies are simply given by non-validity of the linear elastic fracture mechanics approach. In our case of physically short fatigue cracks the level of applied stress is close to cyclic yield stress of the material and, due to large amount of plasticity, conditions of linear elastic fracture mechanics are not satisfied. As a consequence, non-linear elastic plastic fracture mechanics is used for description of the short crack behavior in this article. Concept based on plastic part of J-integral is proposed for the description of the short crack behavior and data obtained for different strain amplitudes are compared. This concept is validated on experimental data obtained on steel 316L.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

21st European Conference on Fracture

ISBN

—

ISSN

2452-3216

e-ISSN

—

Počet stran výsledku

8

Strana od-do

3010-3017

Název nakladatele

Elsevier

Místo vydání

Amsterdam

Místo konání akce

Catania

Datum konání akce

20. 6. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000387976803012