Fracture behaviour of ODS MA956 steel at elevated and high temperatures
Popis výsledku v původním jazyce
Fracture behaviour of oxide dispersion strengthened steel MA956 at elevated and high temperatures is presented. Tensile and fracture toughness tests in the temperature range from 200 to 700°C were performed. The micromechanism of fracture was characterized by fractographic analysis in scanning electron microscope and the dislocations structures under the fracture surfaces were observed in transmission electron microscope. The tensile properties and the fracture toughness properties decrease with increasing temperature. This effect is more pronounced above 400°C. It is connected with the change of fracture micromechanism caused by different dislocation mechanisms.
Název v anglickém jazyce
Fracture behaviour of ODS MA956 steel at elevated and high temperatures
Popis výsledku anglicky
Fracture behaviour of oxide dispersion strengthened steel MA956 at elevated and high temperatures is presented. Tensile and fracture toughness tests in the temperature range from 200 to 700°C were performed. The micromechanism of fracture was characterized by fractographic analysis in scanning electron microscope and the dislocations structures under the fracture surfaces were observed in transmission electron microscope. The tensile properties and the fracture toughness properties decrease with increasing temperature. This effect is more pronounced above 400°C. It is connected with the change of fracture micromechanism caused by different dislocation mechanisms.
Klasifikace
Druh
O - Ostatní výsledky
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů