Effect of C, Ti, Zr and B alloying on fracture mechanisms in hot-rolled Fe-40(at.%)Al
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F09%3A00207250" target="_blank" >RIV/00216208:11320/09:00207250 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68407700:21340/09:00158150
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of C, Ti, Zr and B alloying on fracture mechanisms in hot-rolled Fe-40(at.%)Al
Popis výsledku v původním jazyce
This paper reports a study of fracture behavior of FeAl based intermetallic alloys with addition of carbon, titanium, zirconium and boron (Fe40Al1C, Fe40Al1Ti and Fe40AlZrB). The alloys were prepared by modified processing technology of vacuum inductionmelting and hot rolling in special stainless steel sheath. Tensile and fracture toughness tests were carried out at 20°C, 400°C, 600°C, 700°C and 800°C. The best fracture toughness and tensile properties showed the alloy with Zr and B addition. The fracture toughness at 600°C was comparable with values in stainless steels and nickel-based superalloys. The fractographic analysis revealed the change of fracture micromechanisms with temperature. Moreover, under specific conditions, the fracture micromechanisms were different in tensile and fracture toughness specimens.
Název v anglickém jazyce
Effect of C, Ti, Zr and B alloying on fracture mechanisms in hot-rolled Fe-40(at.%)Al
Popis výsledku anglicky
This paper reports a study of fracture behavior of FeAl based intermetallic alloys with addition of carbon, titanium, zirconium and boron (Fe40Al1C, Fe40Al1Ti and Fe40AlZrB). The alloys were prepared by modified processing technology of vacuum inductionmelting and hot rolling in special stainless steel sheath. Tensile and fracture toughness tests were carried out at 20°C, 400°C, 600°C, 700°C and 800°C. The best fracture toughness and tensile properties showed the alloy with Zr and B addition. The fracture toughness at 600°C was comparable with values in stainless steels and nickel-based superalloys. The fractographic analysis revealed the change of fracture micromechanisms with temperature. Moreover, under specific conditions, the fracture micromechanisms were different in tensile and fracture toughness specimens.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F06%2F0019" target="_blank" >GA106/06/0019: Slitiny na bázi Fe - 40 at.% Al jako základ pro aplikace za vysokých teplot</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Intermetallics
ISSN
0966-9795
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
neuveden
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
—
Kód UT WoS článku
000266900400002
EID výsledku v databázi Scopus
—