Electrochemical corrosion characteristics of phosphated S355J2 steel in sulfate environment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00467769" target="_blank" >RIV/68081723:_____/16:00467769 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.degruyter.com/view/j/kom.2016.60.issue-4/kom-2016-0017/kom-2016-0017.xml" target="_blank" >https://www.degruyter.com/view/j/kom.2016.60.issue-4/kom-2016-0017/kom-2016-0017.xml</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1515/kom-2016-0017" target="_blank" >10.1515/kom-2016-0017</a>

Jazyk výsledku

slovinština

Název v původním jazyce

Elektrochemické korózne charakteristiky fosfátovanej ocele S355J2v prostredí síranov

Popis výsledku v původním jazyce

V priemyselnej praxi sa v súčasnosti využíva veľké množ-stvo spôsobov mechanickej a chemickej predúpravy povrchov ocelí. Výber správnej kombinácie týchto technológií predsta-vuje pre mnoho aplikácií jednu z najdôležitejších úloh. Úče-lom tohto výskumu bolo zhodnotenie vplyvu vybraných spôso-bov mechanickej predúpravy povrchu (brúsenie, otryskávanie pieskom) na kvalitu a elektrochemické korózne charakteristi-ky ocele S355J2 pred a po fi nálnej chemickej úprave povrchu technológiou mangánatého fosfátovania. Povrchová morfoló-gia vytvoreného fosfátu bola hodnotená pomocou rastrovacie-ho elektrónového mikroskopu (REM) a analýza priečneho rezu bola vykonaná na svetelnom metalografi ckom mikroskope. Ako prostredie pre elektrochemické korózne testy bol zvolený roz-tok 0,1M Na2SO4 simulujúci agresívne priemyselné znečistenie. Hodnotenie vplyvu jednotlivých spôsobov mechanickej a che-mickej úpravy povrchu na korózne vlastnosti testovanej ocele bolo vykonané pomocou potenciodynamických polarizačných skúšok (PD) a elektrochemickej impedančnej spektroskopie (EIS) s využitím Tafelovej analýzy a metódy ekvivalentných ob-vodov. Ako ukázali získané výsledky, technológia otryskávania pieskom vplýva negatívne na koróznu odolnosť testovanej oce-le S355J2 i následne vytvorenej vrstvy mangánatého fosfátu.

Název v anglickém jazyce

Electrochemical corrosion characteristics of phosphated S355J2 steel in sulfate environment

Popis výsledku anglicky

Large number of mechanical and chemical surface pretreatment techniques is actually used on steels in industrial practice. Choosing the right combination of these technologies is one of the most important tasks for many applications. The purpose of this research was to evaluate the influence of selected mechanical surface preparation methods (grinding, sandblasting) on the quality and electrochemical corrosion characteristics of S355J2 steel before and after the final chemical surface treatment by the technology of manganese phosphating. The surface morphology of the formed phosphate layer was evaluated by a scanning electron microscopy (SEM) and the cross section analysis was performed by a light metallographic microscopy. 0.1M Na2SO4 solution simulating aggressive industrial pollution was selected for electrochemical corrosion tests. Impact evaluation of various mechanical and chemical surface treatments on the corrosion properties of the tested steel was realized by potentiodynamic polarization tests (PD) and electrochemical impedance spectroscopy (EIS) using the Tafel analysis and equivalent circuits method respectively. The obtained results proved that sandblasting negatively affected the corrosion resistance of S355J2 steel and subsequently created manganese phosphate layer.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Koroze a ochrana materiálu

ISSN

1804-1213

e-ISSN

—

Svazek periodika

60

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

107-113

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85005943876