Study of phosphate formation on S355J2 HSLA steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00479882" target="_blank" >RIV/68081723:_____/17:00479882 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Study of phosphate formation on S355J2 HSLA steel
Popis výsledku v původním jazyce
In present paper, the growth process of the phosphate coating on S355J2 steel was investigated. The microstructure, surface morphology, coating thickness, surface roughness and corrosion resistance of the phosphate coating were analysed by using several techniques including light microscopy, confocal laser scanning microscopy (CLSM) and electrochemical tests - electrochemical impedance spectroscopy (EIS) in 0.1M Na2SO4 solution (simulation of industrial atmosphere). The phosphate coating formation was evaluated after chosen exposure times from 15 minutes to 105 minutes in phosphating bath composed of MnO2, H3PO4 and demineralised H2O. The optimal exposure time of S355J2 steel in selected phosphate solution was determined from surface quality, corrosion resistance and energy consumption point of view.
Název v anglickém jazyce
Study of phosphate formation on S355J2 HSLA steel
Popis výsledku anglicky
In present paper, the growth process of the phosphate coating on S355J2 steel was investigated. The microstructure, surface morphology, coating thickness, surface roughness and corrosion resistance of the phosphate coating were analysed by using several techniques including light microscopy, confocal laser scanning microscopy (CLSM) and electrochemical tests - electrochemical impedance spectroscopy (EIS) in 0.1M Na2SO4 solution (simulation of industrial atmosphere). The phosphate coating formation was evaluated after chosen exposure times from 15 minutes to 105 minutes in phosphating bath composed of MnO2, H3PO4 and demineralised H2O. The optimal exposure time of S355J2 steel in selected phosphate solution was determined from surface quality, corrosion resistance and energy consumption point of view.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
7
Strana od-do
8-14
Kód UT WoS článku
—
EID výsledku v databázi Scopus
2-s2.0-85013754597