Initiation of fatigue cracks and lifetime of Ni-base superalloys at high mean stress and temperature

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00483642" target="_blank" >RIV/68081723:_____/17:00483642 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.prostr.2017.11.059" target="_blank" >http://dx.doi.org/10.1016/j.prostr.2017.11.059</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.prostr.2017.11.059" target="_blank" >10.1016/j.prostr.2017.11.059</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Initiation of fatigue cracks and lifetime of Ni-base superalloys at high mean stress and temperature

Popis výsledku v původním jazyce

The effect of high-frequency cycling (120 Hz) superimposed on high tensile mean stress on a lifetime of cast Ni-base superalloys IN 713LC at 800 °C and MAR-M 247 at 900 °C was investigated. It has been found that both the alloys exhibit qualitatively similar behavior in creep/fatigue loading conditions. Superposition of small stress amplitudes on the tensile mean stress does not influence the time to fracture until the stress amplitude reaches a threshold value, which is dependent on the mean stress. The higher the mean stress the higher is the stress amplitude threshold value. The observed creep/fatigue behavior is governed by two mechanisms: (a) formation and growth of intergranular cracks by creep mechanism (b) initiation and growth of fatigue cracks from the intergranular creep cracks. The casting defects do not play any important role as regards the lifetime under investigated loading conditions.

Název v anglickém jazyce

Initiation of fatigue cracks and lifetime of Ni-base superalloys at high mean stress and temperature

Popis výsledku anglicky

The effect of high-frequency cycling (120 Hz) superimposed on high tensile mean stress on a lifetime of cast Ni-base superalloys IN 713LC at 800 °C and MAR-M 247 at 900 °C was investigated. It has been found that both the alloys exhibit qualitatively similar behavior in creep/fatigue loading conditions. Superposition of small stress amplitudes on the tensile mean stress does not influence the time to fracture until the stress amplitude reaches a threshold value, which is dependent on the mean stress. The higher the mean stress the higher is the stress amplitude threshold value. The observed creep/fatigue behavior is governed by two mechanisms: (a) formation and growth of intergranular cracks by creep mechanism (b) initiation and growth of fatigue cracks from the intergranular creep cracks. The casting defects do not play any important role as regards the lifetime under investigated loading conditions.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

<a href="/cs/project/EG15_019%2F0004399" target="_blank" >EG15_019/0004399: Výzkum a vývoj technologií přesného lití nových typů odlitků leteckých motorů a integrálně litých axiálních kol turbodmychadel</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

3RD INTERNATIONAL SYMPOSIUM ON FATIGUE DESIGN AND MATERIAL DEFECTS (FDMD 2017)

ISBN

—

ISSN

2452-3216

e-ISSN

—

Počet stran výsledku

6

Strana od-do

44-49

Název nakladatele

Elsevier

Místo vydání

Amsterdam

Místo konání akce

Lecco

Datum konání akce

19. 9. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000452909100007