Preparation and characterization of novel environmentally friendly Al2O3/SiO2/CaO ceramic foams

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00494817" target="_blank" >RIV/68081723:_____/18:00494817 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/18:PU128580

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.ceramint.2018.07.107" target="_blank" >http://dx.doi.org/10.1016/j.ceramint.2018.07.107</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ceramint.2018.07.107" target="_blank" >10.1016/j.ceramint.2018.07.107</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and characterization of novel environmentally friendly Al2O3/SiO2/CaO ceramic foams

Popis výsledku v původním jazyce

Low-cost Al2O3-SiO2-CaO ceramic foams were prepared using a novel and simple reactive foaming process. The foamed green bodies were produced by mixing aluminium powder and calcium hydroxide in an aqueous solution of sodium silicate and sintered in an argon atmosphere using a pressureless electric current assisted process (T = 800 C). An additional thermal treatment was performed in air using a conventional furnace (T = 1050 degrees C) in order to oxidize the residual metallic phases. The resulting foams exhibited open porosity, densities ranging from 0.50 to 0.65 g/cm(3) and wide pore size distribution (0.04-400 mu m). The compressive strength and thermal diffusivity of these foams ranged from 2.12 to 1.01 MPa and from 0.27 to 0.45 mm(2)s(-1), respectively, which indicate their suitability as thermal insulator materials.

Název v anglickém jazyce

Preparation and characterization of novel environmentally friendly Al2O3/SiO2/CaO ceramic foams

Popis výsledku anglicky

Low-cost Al2O3-SiO2-CaO ceramic foams were prepared using a novel and simple reactive foaming process. The foamed green bodies were produced by mixing aluminium powder and calcium hydroxide in an aqueous solution of sodium silicate and sintered in an argon atmosphere using a pressureless electric current assisted process (T = 800 C). An additional thermal treatment was performed in air using a conventional furnace (T = 1050 degrees C) in order to oxidize the residual metallic phases. The resulting foams exhibited open porosity, densities ranging from 0.50 to 0.65 g/cm(3) and wide pore size distribution (0.04-400 mu m). The compressive strength and thermal diffusivity of these foams ranged from 2.12 to 1.01 MPa and from 0.27 to 0.45 mm(2)s(-1), respectively, which indicate their suitability as thermal insulator materials.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

<a href="/cs/project/GJ17-08447Y" target="_blank" >GJ17-08447Y: Výpočtové modelování porušování vysoce porézních keramických materiálů s reálnými výrobními defekty</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics International

ISSN

0272-8842

e-ISSN

—

Svazek periodika

44

Číslo periodika v rámci svazku

15

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

19063-19069

Kód UT WoS článku

000445993000192

EID výsledku v databázi Scopus

2-s2.0-85050105219