Engineering properties of alkali activated fly ash foams

Popis výsledku v původním jazyce

Inorganic foams were prepared from alkali activated fly ash and aluminum powder blowing agent. Curing process was accelerated by thermal treatment at 80 °C for 12 hours. Bulk densities ranged between 420 and 800 kg/m3, depending on batch proportions. Compressive strength was found in the range 3.7-9.0 MPa, Young's modulus 0.6-1.1 GPa, thermal conductivity 0.14-0.16 W/m/K. Young?s modulus was reproduced using 2D numerical simulations and analytical homogenizations.

Název v anglickém jazyce

Engineering properties of alkali activated fly ash foams

Popis výsledku anglicky

Inorganic foams were prepared from alkali activated fly ash and aluminum powder blowing agent. Curing process was accelerated by thermal treatment at 80 °C for 12 hours. Bulk densities ranged between 420 and 800 kg/m3, depending on batch proportions. Compressive strength was found in the range 3.7-9.0 MPa, Young's modulus 0.6-1.1 GPa, thermal conductivity 0.14-0.16 W/m/K. Young?s modulus was reproduced using 2D numerical simulations and analytical homogenizations.

Druh

O - Ostatní výsledky

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.30.0034" target="_blank" >EE2.3.30.0034: Podpora zkvalitnění týmů výzkumu a vývoje a rozvoj intersektorální mobility na ČVUT v Praze</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů