Radiation damage evolution in High Entropy Alloys (HEAs) caused by 3–5 MeV Au and 5 MeV Cu ions in a broad range of dpa in connection to mechanical properties and internal morphology

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F23%3A00577605" target="_blank" >RIV/68081723:_____/23:00577605 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/23:00577605 RIV/61389021:_____/23:00577605 RIV/61389005:_____/23:00577605 RIV/68407700:21340/23:00369620 a 2 dalších

Výsledek na webu

<a href="https://doi.org/10.1016/j.nme.2023.101510" target="_blank" >https://doi.org/10.1016/j.nme.2023.101510</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.nme.2023.101510" target="_blank" >10.1016/j.nme.2023.101510</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Radiation damage evolution in High Entropy Alloys (HEAs) caused by 3–5 MeV Au and 5 MeV Cu ions in a broad range of dpa in connection to mechanical properties and internal morphology

Popis výsledku v původním jazyce

High Entropy Alloys (HEAs) are prospective materials for nuclear fusion reactors and were irradiated in this study at a broad range of energetic ion fluences. Different ion masses (Cu and Au ions) and energies (3 and 5 MeV) were selected to investigate dpa (displacement per atom) development, radiation defect accumulation based on prevailing collision processes (Au ions) and ionization processes (Cu ions) in various HEAs. The studied HEAs differ in terms of elemental composition, internal morphology (grain structure) and other modifiers. Dpa values of 1 to similar to 66 were achieved at Cu and Au ion fluences from 4 x 10(14) to 1.3 x 10(16) ions.cm(-2) at room temperature, which generated varying levels of lattice damage. Theoretical simulations were performed to es-timate the energy stopping and dpa depth distribution using SRIM code and compared with Au-concentration depth profiles determined by Rutherford backscattering spectrometry for Au-ions with 3 MeV ion energy. The prevailing energy losses of ions via ionization processes for Cu-5 MeV ions were found to increase the damage through lattice strain and probable lattice distortion, although the main defect introduction is expected to occur via collisions during nuclear stopping. Structural modification and defect accumulation were investigated by positron annihilation spectroscopy (PAS), which revealed a broader damaged layer with defects, where HEA-Nb (NbCrFeMnNi) exhibited the least damage accumulation from chosen alloys with no strong relation to the Au-5 MeV ion implantation fluence, whereas strong defect accumulation was recorded in the Au-ion implanted Eurofer97 used for comparison and HEA-Co (CoCrFeMnNi). PAS analysis also allowed defect sizes to be deter-mined as an additional structural characteristic. The observed trends were also confirmed by thermal property analysis, with a worsening of thermal effusivity recorded after the irradiation in HEA-Co and Eurofer97. The worsening of the thermal properties was confirmed by the layer thickness, where the layer identified by PAS was found to be broader than the SRIM theoretical predictions. Nanoindentation measurements confirmed less pronounced radiation hardening of HEA-Nb relative to that observed in HEA-Co and Eurofer97. Transmission Electron Microscopy (TEM) analysis revealed layer thicknesses in reasonable agreement with the dpa depth profiles. The thermal effusivity decreased in the surface-irradiated layer in all investigated samples, the least influenced material was HEA-Nb.

Název v anglickém jazyce

Radiation damage evolution in High Entropy Alloys (HEAs) caused by 3–5 MeV Au and 5 MeV Cu ions in a broad range of dpa in connection to mechanical properties and internal morphology

Popis výsledku anglicky

High Entropy Alloys (HEAs) are prospective materials for nuclear fusion reactors and were irradiated in this study at a broad range of energetic ion fluences. Different ion masses (Cu and Au ions) and energies (3 and 5 MeV) were selected to investigate dpa (displacement per atom) development, radiation defect accumulation based on prevailing collision processes (Au ions) and ionization processes (Cu ions) in various HEAs. The studied HEAs differ in terms of elemental composition, internal morphology (grain structure) and other modifiers. Dpa values of 1 to similar to 66 were achieved at Cu and Au ion fluences from 4 x 10(14) to 1.3 x 10(16) ions.cm(-2) at room temperature, which generated varying levels of lattice damage. Theoretical simulations were performed to es-timate the energy stopping and dpa depth distribution using SRIM code and compared with Au-concentration depth profiles determined by Rutherford backscattering spectrometry for Au-ions with 3 MeV ion energy. The prevailing energy losses of ions via ionization processes for Cu-5 MeV ions were found to increase the damage through lattice strain and probable lattice distortion, although the main defect introduction is expected to occur via collisions during nuclear stopping. Structural modification and defect accumulation were investigated by positron annihilation spectroscopy (PAS), which revealed a broader damaged layer with defects, where HEA-Nb (NbCrFeMnNi) exhibited the least damage accumulation from chosen alloys with no strong relation to the Au-5 MeV ion implantation fluence, whereas strong defect accumulation was recorded in the Au-ion implanted Eurofer97 used for comparison and HEA-Co (CoCrFeMnNi). PAS analysis also allowed defect sizes to be deter-mined as an additional structural characteristic. The observed trends were also confirmed by thermal property analysis, with a worsening of thermal effusivity recorded after the irradiation in HEA-Co and Eurofer97. The worsening of the thermal properties was confirmed by the layer thickness, where the layer identified by PAS was found to be broader than the SRIM theoretical predictions. Nanoindentation measurements confirmed less pronounced radiation hardening of HEA-Nb relative to that observed in HEA-Co and Eurofer97. Transmission Electron Microscopy (TEM) analysis revealed layer thicknesses in reasonable agreement with the dpa depth profiles. The thermal effusivity decreased in the surface-irradiated layer in all investigated samples, the least influenced material was HEA-Nb.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nuclear Materials and Energy

ISSN

2352-1791

e-ISSN

2352-1791

Svazek periodika

37

Číslo periodika v rámci svazku

DEC

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

16

Strana od-do

101510

Kód UT WoS článku

001084471800001

EID výsledku v databázi Scopus

2-s2.0-85171423895