Oxidation of graphite-like carbon films with different microhardness and density.

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F03%3A02030277" target="_blank" >RIV/68378271:_____/03:02030277 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Oxidation of graphite-like carbon films with different microhardness and density.
Popis výsledku v původním jazyce
Evolution of microhardness, internal stress and thickness of three types of carbon(a-C) films(#1-3) with different microhardness (H=60, 24, and 20 GPa) and density after annealing in air for 1 h temperatures of 100, 200, 300, 350 and 400 o C was investigated. The film obtained has a graphite-like structure and its composition corresponds approximately to formula CO 0.15 -CO 0.18 .
Název v anglickém jazyce
Oxidation of graphite-like carbon films with different microhardness and density.
Popis výsledku anglicky
Evolution of microhardness, internal stress and thickness of three types of carbon(a-C) films(#1-3) with different microhardness (H=60, 24, and 20 GPa) and density after annealing in air for 1 h temperatures of 100, 200, 300, 350 and 400 o C was investigated. The film obtained has a graphite-like structure and its composition corresponds approximately to formula CO 0.15 -CO 0.18 .

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2003
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)