Enhancing nanocrystalline diamond surface conductivity by deposition temperature and chemical post-processing

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F09%3A00332489" target="_blank" >RIV/68378271:_____/09:00332489 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Enhancing nanocrystalline diamond surface conductivity by deposition temperature and chemical post-processing

Popis výsledku v původním jazyce

The surface conductivity of nanocrystalline diamond (NCD) films as a function of deposition temperature and chemical post-processing was characterized by current-voltage measurements using co-planar Au electrodes. Raman spectroscopy was applied to investigate the bulk quality of NCD films. The surface material properties and morphology were studied using atomic force microscopy (AFM). The results indicate that the chemical post-processing of as-grown NCD films and re-hydrogenation leads to a significantincrease in the surface conductivity by three orders of magnitude. The highest surface conductivity was obtained on NCD films deposited at 600°C.

Název v anglickém jazyce

Enhancing nanocrystalline diamond surface conductivity by deposition temperature and chemical post-processing

Popis výsledku anglicky

The surface conductivity of nanocrystalline diamond (NCD) films as a function of deposition temperature and chemical post-processing was characterized by current-voltage measurements using co-planar Au electrodes. Raman spectroscopy was applied to investigate the bulk quality of NCD films. The surface material properties and morphology were studied using atomic force microscopy (AFM). The results indicate that the chemical post-processing of as-grown NCD films and re-hydrogenation leads to a significantincrease in the surface conductivity by three orders of magnitude. The highest surface conductivity was obtained on NCD films deposited at 600°C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica Status Solidi. A

ISSN

1862-6300

e-ISSN

—

Svazek periodika

206

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000264009900017

EID výsledku v databázi Scopus

—