Hot rolling and annealing of cast Fe-Al-Si-C alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00353228" target="_blank" >RIV/68378271:_____/10:00353228 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/10:86075766

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hot rolling and annealing of cast Fe-Al-Si-C alloy

Popis výsledku v původním jazyce

The iron aluminides with an increased content of silicon and carbon are used for structural purposes in the cast state. A special method of hot rolling of laboratory castings from the alloy Fe ? 29.5 Al ? 0.47 Si ? 1.16 C (wt. %) was developed, preventing the origin of surface cracks in contact with the cold work rolls and enabling forming this material with the extremely low plasticity. The structure of the initial castings is characterized by a large heterogeneity, as far as mainly the distribution, shape, size and orientation of carbides Al4C3 is concerned. After the multi-pass hot rolling, the structure with grains stretched in the direction of rolling was achieved. The long-term annealing at temperature 1200 °C led progressively to crumbling of the greatest formations and, vice versa, coarsening of the finest grains. The present aluminium carbides hamper the static recrystallization of the investigated material very effectively.

Název v anglickém jazyce

Hot rolling and annealing of cast Fe-Al-Si-C alloy

Popis výsledku anglicky

The iron aluminides with an increased content of silicon and carbon are used for structural purposes in the cast state. A special method of hot rolling of laboratory castings from the alloy Fe ? 29.5 Al ? 0.47 Si ? 1.16 C (wt. %) was developed, preventing the origin of surface cracks in contact with the cold work rolls and enabling forming this material with the extremely low plasticity. The structure of the initial castings is characterized by a large heterogeneity, as far as mainly the distribution, shape, size and orientation of carbides Al4C3 is concerned. After the multi-pass hot rolling, the structure with grains stretched in the direction of rolling was achieved. The long-term annealing at temperature 1200 °C led progressively to crumbling of the greatest formations and, vice versa, coarsening of the finest grains. The present aluminium carbides hamper the static recrystallization of the investigated material very effectively.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F10%2F0438" target="_blank" >GAP107/10/0438: Fyzikální a metalurgické aspekty deformačního chování aluminidů železa s extrémně nízkou plasticitou</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

63

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—