Crystal growth and scintillation characteristics of the Nd3+ doped LaF3 single crystal

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F10%3A00353472" target="_blank" >RIV/68378271:_____/10:00353472 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Crystal growth and scintillation characteristics of the Nd3+ doped LaF3 single crystal
Popis výsledku v původním jazyce
Two-inch diameter Nd3+ doped LaF3 single crystals were successfully grown by the Czochralski technique. No remarkable absorption due to unfavorable impurities or color centers was observed from optical absorption measurements in the vacuum ultra-violet spectral region. The high crystallinity and homogeneous Nd3+ distribution were found from X-ray rocking curve and chemical composition analysis, respectively. X-ray excited luminescence spectrum was measured and the significant 4f25d?4f3 luminescence at 173 nm was observed in the grown crystal.
Název v anglickém jazyce
Crystal growth and scintillation characteristics of the Nd3+ doped LaF3 single crystal
Popis výsledku anglicky
Two-inch diameter Nd3+ doped LaF3 single crystals were successfully grown by the Czochralski technique. No remarkable absorption due to unfavorable impurities or color centers was observed from optical absorption measurements in the vacuum ultra-violet spectral region. The high crystallinity and homogeneous Nd3+ distribution were found from X-ray rocking curve and chemical composition analysis, respectively. X-ray excited luminescence spectrum was measured and the significant 4f25d?4f3 luminescence at 173 nm was observed in the grown crystal.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)