Luminescence and scintillation properties of advanced Lu3Al5O12:Pr3+ single crystal scintillators

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F14%3A00432400" target="_blank" >RIV/68378271:_____/14:00432400 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.radmeas.2013.11.009" target="_blank" >http://dx.doi.org/10.1016/j.radmeas.2013.11.009</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.radmeas.2013.11.009" target="_blank" >10.1016/j.radmeas.2013.11.009</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Luminescence and scintillation properties of advanced Lu3Al5O12:Pr3+ single crystal scintillators

Popis výsledku v původním jazyce

We present the luminescence and scintillation properties of Lu3Al5O12:Pr (LuAG:Pr) single crystals with Pr3? concentration of 0.13 wt %, grown by the Czochralski method. The light yield and energy resolution were measured under 662 keV g-ray excitation.The dominant emission band peaking at 310 nm with a shoulder at 370 nm was observed in the photoluminescence spectrum. High light yield of 24,500 ph/MeV and an energy resolution of 5.3 % were obtained for a 6 x 6 x 2 mm3 LuAG:Pr sample. Light yield dependence on sample height and shaping time was measured. The estimated photofraction in pulse height spectrum and total mass attenuation coefficient at 662 keV g-rays were also determined.

Název v anglickém jazyce

Luminescence and scintillation properties of advanced Lu3Al5O12:Pr3+ single crystal scintillators

Popis výsledku anglicky

We present the luminescence and scintillation properties of Lu3Al5O12:Pr (LuAG:Pr) single crystals with Pr3? concentration of 0.13 wt %, grown by the Czochralski method. The light yield and energy resolution were measured under 662 keV g-ray excitation.The dominant emission band peaking at 310 nm with a shoulder at 370 nm was observed in the photoluminescence spectrum. High light yield of 24,500 ph/MeV and an energy resolution of 5.3 % were obtained for a 6 x 6 x 2 mm3 LuAG:Pr sample. Light yield dependence on sample height and shaping time was measured. The estimated photofraction in pulse height spectrum and total mass attenuation coefficient at 662 keV g-rays were also determined.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP204%2F12%2F0805" target="_blank" >GAP204/12/0805: Pokročilá materiálová řešení pro tenkovrstvé scintilátory a transformátory světla</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Radiation Measurements

ISSN

1350-4487

e-ISSN

—

Svazek periodika

60

Číslo periodika v rámci svazku

Jan

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

4

Strana od-do

42-45

Kód UT WoS článku

000331162200008

EID výsledku v databázi Scopus

—