Corrosion of NiTi wires with cracked oxide layer
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F14%3A00432510" target="_blank" >RIV/68378271:_____/14:00432510 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61388998:_____/14:00432510
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s11665-014-0925-8" target="_blank" >http://dx.doi.org/10.1007/s11665-014-0925-8</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11665-014-0925-8" target="_blank" >10.1007/s11665-014-0925-8</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Corrosion of NiTi wires with cracked oxide layer
Popis výsledku v původním jazyce
Corrosion behavior of superelastic NiTi shape memory alloy wires with cracked TiO2 surface oxide layers was investigated by electrochemical corrosion tests (Electrochemical Impedance Spectroscopy, Open Circuit Potential, and Potentiodynamic Polarization)on wires bent into U-shapes of various bending radii. Cracks within the oxide on the surface of the bent wires were observed by FIB?SEM and TEM methods. The density and width of the surface oxide cracks dramatically increase with decreasing bending radius. The results of electrochemical experiments consistently show that corrosion properties of NiTi wires with cracked oxide layers (static load keeps the cracks opened) are inferior compared to the corrosion properties of the straight NiTi wires coveredby virgin uncracked oxides.
Název v anglickém jazyce
Corrosion of NiTi wires with cracked oxide layer
Popis výsledku anglicky
Corrosion behavior of superelastic NiTi shape memory alloy wires with cracked TiO2 surface oxide layers was investigated by electrochemical corrosion tests (Electrochemical Impedance Spectroscopy, Open Circuit Potential, and Potentiodynamic Polarization)on wires bent into U-shapes of various bending radii. Cracks within the oxide on the surface of the bent wires were observed by FIB?SEM and TEM methods. The density and width of the surface oxide cracks dramatically increase with decreasing bending radius. The results of electrochemical experiments consistently show that corrosion properties of NiTi wires with cracked oxide layers (static load keeps the cracks opened) are inferior compared to the corrosion properties of the straight NiTi wires coveredby virgin uncracked oxides.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Materials Engineering and Performance
ISSN
1059-9495
e-ISSN
—
Svazek periodika
23
Číslo periodika v rámci svazku
7
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
10
Strana od-do
2659-2668
Kód UT WoS článku
000339010700054
EID výsledku v databázi Scopus
—