Mechanically induced demagnetization and remanent magnetization rotation in Ni-Mn-Ga (-B) magnetic shape memory alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F14%3A00434049" target="_blank" >RIV/68378271:_____/14:00434049 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S1359646214002176" target="_blank" >http://www.sciencedirect.com/science/article/pii/S1359646214002176</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2014.05.017" target="_blank" >10.1016/j.scriptamat.2014.05.017</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanically induced demagnetization and remanent magnetization rotation in Ni-Mn-Ga (-B) magnetic shape memory alloy

Popis výsledku v původním jazyce

Boron doping increased the magnetic coercivity from 1.5 to 22 kA m(-1) (19 to 276 Oe) in Ni-50 Mn28.5Ga21.5 single crystals, which in combination with the multiferroic character of the material resulted in interesting new magnetomechanical effects. The material behaved as a semi-hard ferromagnet, which-in contrast to conventional ferromagnets-could be demagnetized by applying light (2 MPa) mechanical loading. We envisage that remanent magnetization rotation by magnetic field or by mechanical stress canoccur if the hysteresis is further enlarged.

Název v anglickém jazyce

Mechanically induced demagnetization and remanent magnetization rotation in Ni-Mn-Ga (-B) magnetic shape memory alloy

Popis výsledku anglicky

Boron doping increased the magnetic coercivity from 1.5 to 22 kA m(-1) (19 to 276 Oe) in Ni-50 Mn28.5Ga21.5 single crystals, which in combination with the multiferroic character of the material resulted in interesting new magnetomechanical effects. The material behaved as a semi-hard ferromagnet, which-in contrast to conventional ferromagnets-could be demagnetized by applying light (2 MPa) mechanical loading. We envisage that remanent magnetization rotation by magnetic field or by mechanical stress canoccur if the hysteresis is further enlarged.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F11%2F0391" target="_blank" >GAP107/11/0391: Heuslerovy slitiny vykazující jev magnetické tvarové paměti a příbuzné jevy</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

87

Číslo periodika v rámci svazku

SEP

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

25-28

Kód UT WoS článku

000339701300007

EID výsledku v databázi Scopus

—