The influence of Sn Additions on the Thermoelectric and Transport Properties of FeSb2Te-based Ternary Skutterudites
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F16%3A00459335" target="_blank" >RIV/68378271:_____/16:00459335 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61389013:_____/16:00459335 RIV/00216275:25310/16:39901158
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s11664-015-4325-0" target="_blank" >http://dx.doi.org/10.1007/s11664-015-4325-0</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11664-015-4325-0" target="_blank" >10.1007/s11664-015-4325-0</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The influence of Sn Additions on the Thermoelectric and Transport Properties of FeSb2Te-based Ternary Skutterudites
Popis výsledku v původním jazyce
The influence of Sn additions was studied in a series of samples of a nominal composition FeSb2Te(1-x)Sn(x) (x=0, 0.05, 0.1, 0.15, 0.2). SnTe compound was primarily identified in the matrix compound of the ternary skutterudite structure in the multiphase composite samples. A detailed analysis of the composition of the ternary skutterudite matrix revealed the crucial role of the Sb/Te ratio as the dominant factor driving the observed changes of the measured properties. The anomalous changes of the measured transport properties values were explained in terms of an effective medium theory for two-phase FeSb2Te-SnTe composites. A maximum value of thermoelectric figure-of-merit ZT=0.47 at 673 K was attained for the sample of a nominal composition FeSb2Te0.85Sn0.15.
Název v anglickém jazyce
The influence of Sn Additions on the Thermoelectric and Transport Properties of FeSb2Te-based Ternary Skutterudites
Popis výsledku anglicky
The influence of Sn additions was studied in a series of samples of a nominal composition FeSb2Te(1-x)Sn(x) (x=0, 0.05, 0.1, 0.15, 0.2). SnTe compound was primarily identified in the matrix compound of the ternary skutterudite structure in the multiphase composite samples. A detailed analysis of the composition of the ternary skutterudite matrix revealed the crucial role of the Sb/Te ratio as the dominant factor driving the observed changes of the measured properties. The anomalous changes of the measured transport properties values were explained in terms of an effective medium theory for two-phase FeSb2Te-SnTe composites. A maximum value of thermoelectric figure-of-merit ZT=0.47 at 673 K was attained for the sample of a nominal composition FeSb2Te0.85Sn0.15.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA13-33056S" target="_blank" >GA13-33056S: Charakterizace tenkých termoelektrických vrstev a multi-vrstevnatých struktur pomocí rastrovacího termálního mikroskopu a Harmanovy metody.</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Electronic Materials
ISSN
0361-5235
e-ISSN
—
Svazek periodika
45
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
10
Strana od-do
2904-2913
Kód UT WoS článku
000375074700036
EID výsledku v databázi Scopus
2-s2.0-84954088544