Transformation of ZnO-based structures under heavy Mo doping: Defect states and luminescence

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F21%3A00557518" target="_blank" >RIV/68378271:_____/21:00557518 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68407700:21230/21:00362900 RIV/68407700:21340/21:00362900
Výsledek na webu
<a href="https://www.confer.cz/nanocon/2021/download/4321-transformation-of-zno-based-structures-under-heavy-mo-doping-defect-states-and-luminescence.pdf" target="_blank" >https://www.confer.cz/nanocon/2021/download/4321-transformation-of-zno-based-structures-under-heavy-mo-doping-defect-states-and-luminescence.pdf</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.37904/nanocon.2021.4321" target="_blank" >10.37904/nanocon.2021.4321</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Transformation of ZnO-based structures under heavy Mo doping: Defect states and luminescence
Popis výsledku v původním jazyce
Hydrothermally grown ZnO-based structures were heavily doped with Mo (various doping levels from 2 to 25%). It has been found that Mo strongly affects the ZnO structure and morphology rather resulting in the complex, mixed zinc and molybdenum oxides creation. Moreover, the material phases transformation upon the increased Mo content was observed. ZnO material phase was observed only at low Mo doping level (2 and 5%). This correlated very well to the changes in the luminescence and electron paramagnetic resonance signals.
Název v anglickém jazyce
Transformation of ZnO-based structures under heavy Mo doping: Defect states and luminescence
Popis výsledku anglicky
Hydrothermally grown ZnO-based structures were heavily doped with Mo (various doping levels from 2 to 25%). It has been found that Mo strongly affects the ZnO structure and morphology rather resulting in the complex, mixed zinc and molybdenum oxides creation. Moreover, the material phases transformation upon the increased Mo content was observed. ZnO material phase was observed only at low Mo doping level (2 and 5%). This correlated very well to the changes in the luminescence and electron paramagnetic resonance signals.

Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt
<a href="/cs/project/GJ20-05497Y" target="_blank" >GJ20-05497Y: Nanoscintilátory na bázi ultrarychlých luminiscenčních struktur tvořených násobnými kvantovými jamami a komposity</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)