Merging of Bi-modality of ultrafast laser processing: Heating of Si/Au nanocomposite solutions with controlled chemical content

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F24%3A00584335" target="_blank" >RIV/68378271:_____/24:00584335 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22340/24:43928422

Výsledek na webu

<a href="https://hdl.handle.net/11104/0352258" target="_blank" >https://hdl.handle.net/11104/0352258</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/nano14040321" target="_blank" >10.3390/nano14040321</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Merging of Bi-modality of ultrafast laser processing: Heating of Si/Au nanocomposite solutions with controlled chemical content

Popis výsledku v původním jazyce

Ultrafast laser processing possesses unique outlooks for the synthesis of novel nanoarchi- tectures and their further applications in the field of life science. It allows not only the formation of multi-element nanostructures with tuneable performance but also provides various non-invasive laser-stimulated modalities. In this work, we employed ultrafast laser processing for the manufac- turing of silicon–gold nanocomposites (Si/Au NCs) with the Au mass fraction variable from 15% (0.5 min ablation time) to 79% (10 min) which increased their plasmonic efficiency by six times and narrowed the bandgap from 1.55 eV to 1.23 eV. These nanostructures demonstrated a considerable fs laser-stimulated hyperthermia with a Au-dependent heating efficiency (~10–20 ◦C). The prepared surfactant-free colloidal solutions showed good chemical stability with a decrease (i) of zeta (ξ) potential (from −46 mV to −30 mV) and (ii) of the hydrodynamic size of the nanoparticles (from 104 nm to 52 nm) due to the increase in the laser ablation time from 0.5 min to 10 min. The electrical conductivity of NCs revealed a minimum value (~1.53 µS/cm) at 2 min ablation time while their increasing concentration was saturated (~1012 NPs/mL) at 7 min ablation duration. The formed NCs demonstrated a polycrystalline Au nature regardless of the laser ablation time accompanied with the coexistence of oxidized Au and oxidized Si as well as gold silicide phases at a shorter laser ablation time (<1 min) and the formation of a pristine Au at a longer irradiation. Our findings demonstrate the merged employment of ultrafast laser processing for the design of multi-element NCs with tuneable properties reveal efficient composition-sensitive photo-thermal therapy modality.

Název v anglickém jazyce

Merging of Bi-modality of ultrafast laser processing: Heating of Si/Au nanocomposite solutions with controlled chemical content

Popis výsledku anglicky

Ultrafast laser processing possesses unique outlooks for the synthesis of novel nanoarchi- tectures and their further applications in the field of life science. It allows not only the formation of multi-element nanostructures with tuneable performance but also provides various non-invasive laser-stimulated modalities. In this work, we employed ultrafast laser processing for the manufac- turing of silicon–gold nanocomposites (Si/Au NCs) with the Au mass fraction variable from 15% (0.5 min ablation time) to 79% (10 min) which increased their plasmonic efficiency by six times and narrowed the bandgap from 1.55 eV to 1.23 eV. These nanostructures demonstrated a considerable fs laser-stimulated hyperthermia with a Au-dependent heating efficiency (~10–20 ◦C). The prepared surfactant-free colloidal solutions showed good chemical stability with a decrease (i) of zeta (ξ) potential (from −46 mV to −30 mV) and (ii) of the hydrodynamic size of the nanoparticles (from 104 nm to 52 nm) due to the increase in the laser ablation time from 0.5 min to 10 min. The electrical conductivity of NCs revealed a minimum value (~1.53 µS/cm) at 2 min ablation time while their increasing concentration was saturated (~1012 NPs/mL) at 7 min ablation duration. The formed NCs demonstrated a polycrystalline Au nature regardless of the laser ablation time accompanied with the coexistence of oxidized Au and oxidized Si as well as gold silicide phases at a shorter laser ablation time (<1 min) and the formation of a pristine Au at a longer irradiation. Our findings demonstrate the merged employment of ultrafast laser processing for the design of multi-element NCs with tuneable properties reveal efficient composition-sensitive photo-thermal therapy modality.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10306 - Optics (including laser optics and quantum optics)

Projekt

<a href="/cs/project/EH22_008%2F0004596" target="_blank" >EH22_008/0004596: Senzory a detektory pro informační společnost budoucnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2024

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nanomaterials

ISSN

2079-4991

e-ISSN

2079-4991

Svazek periodika

14

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

16

Strana od-do

321

Kód UT WoS článku

001173082700001

EID výsledku v databázi Scopus

2-s2.0-85185657525