Effect of surface layer depth on fatigue life of carburized steel and analysis of fracture proces

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F12%3A00382344" target="_blank" >RIV/68378297:_____/12:00382344 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of surface layer depth on fatigue life of carburized steel and analysis of fracture proces

Popis výsledku v původním jazyce

Nowadays, it has been strongly required to extend the fatigue life of machine components and structures due to economic. To meet this demand, various surface refining processes have become major interest because they can provide additional surface properties such as high strength, thermal barrier, corrosion and wear resistance to structural materials. One of the most commonly used refining techniques is carburizing. The depth of carburized layer is one of the most important parameters determining fatigue endurance of machine components. This work deals with fatigue life dependence on carburized layer depth.

Název v anglickém jazyce

Effect of surface layer depth on fatigue life of carburized steel and analysis of fracture proces

Popis výsledku anglicky

Nowadays, it has been strongly required to extend the fatigue life of machine components and structures due to economic. To meet this demand, various surface refining processes have become major interest because they can provide additional surface properties such as high strength, thermal barrier, corrosion and wear resistance to structural materials. One of the most commonly used refining techniques is carburizing. The depth of carburized layer is one of the most important parameters determining fatigue endurance of machine components. This work deals with fatigue life dependence on carburized layer depth.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Fracture mechanics of durability, reliability and safety

ISBN

978-5-905576-18-8

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

224-231

Název nakladatele

Foliant Kazan

Místo vydání

Kazan

Místo konání akce

Kazan

Datum konání akce

26. 8. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—