Crystallization of aragonite from vaterite precursor during various refluxing times
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F15%3A00444695" target="_blank" >RIV/68378297:_____/15:00444695 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.scientific.net/AMR.1119.466" target="_blank" >http://www.scientific.net/AMR.1119.466</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.1119.466" target="_blank" >10.4028/www.scientific.net/AMR.1119.466</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crystallization of aragonite from vaterite precursor during various refluxing times
Popis výsledku v původním jazyce
CaCO3 polymorphs are intensively studied due to their importance in the nature and the widespread use in the industry as well. This work is dealing with the crystallization of aragonite from vaterite dispersion during the refluxation at 100°C. The characterization of CaCO3 polymorphs during vaterite transformation was performed with Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and X-ray powder diffraction (XRPD). The influence of the different refluxing times on thearagonite crystallization was discussed. The purest aragonite, 70.7(2) wt.%, was synthetized in the sample refluxed for 60 minutes. Prolonged refluxation strongly affected aragonite crystals with gradual transformation into calcite.
Název v anglickém jazyce
Crystallization of aragonite from vaterite precursor during various refluxing times
Popis výsledku anglicky
CaCO3 polymorphs are intensively studied due to their importance in the nature and the widespread use in the industry as well. This work is dealing with the crystallization of aragonite from vaterite dispersion during the refluxation at 100°C. The characterization of CaCO3 polymorphs during vaterite transformation was performed with Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and X-ray powder diffraction (XRPD). The influence of the different refluxing times on thearagonite crystallization was discussed. The purest aragonite, 70.7(2) wt.%, was synthetized in the sample refluxed for 60 minutes. Prolonged refluxation strongly affected aragonite crystals with gradual transformation into calcite.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advanced materials research
ISBN
978-3-03835-513-7
ISSN
1022-6680
e-ISSN
—
Počet stran výsledku
5
Strana od-do
466-470
Název nakladatele
Trans Tech Publications
Místo vydání
Zürich
Místo konání akce
Singapur
Datum konání akce
21. 3. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—