Role of compactness on hardness and reduced modulus of vaterite determined with nanoindentation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F19%3A00505997" target="_blank" >RIV/68378297:_____/19:00505997 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1007/978-3-030-21894-2_1" target="_blank" >https://doi.org/10.1007/978-3-030-21894-2_1</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/978-3-030-21894-2_1" target="_blank" >10.1007/978-3-030-21894-2_1</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Role of compactness on hardness and reduced modulus of vaterite determined with nanoindentation

Popis výsledku v původním jazyce

The influence of compaction degree of synthetic vaterite, the metastable polymorph of calcium carbonate, on determined mechanical properties was investigated using nanoindentation instrument. Specimens for measurements were prepared as pressed pellets with the application of three different forces—40, 60 and 80 kN. The highest values of reduced modulus and hardness were detected for vateritic pellet pressed at 60 kN. For this specimen, reduced modulus and hardness were found to be in ranges 74–10 and 5.2–0.3 GPa, respectively. Observation with scanning electron microscope showed increase compactness of pellet’s microstructure and an increase in density and length of microcracks within vateritic pellets when higher pressing force was applied.

Název v anglickém jazyce

Role of compactness on hardness and reduced modulus of vaterite determined with nanoindentation

Popis výsledku anglicky

The influence of compaction degree of synthetic vaterite, the metastable polymorph of calcium carbonate, on determined mechanical properties was investigated using nanoindentation instrument. Specimens for measurements were prepared as pressed pellets with the application of three different forces—40, 60 and 80 kN. The highest values of reduced modulus and hardness were detected for vateritic pellet pressed at 60 kN. For this specimen, reduced modulus and hardness were found to be in ranges 74–10 and 5.2–0.3 GPa, respectively. Observation with scanning electron microscope showed increase compactness of pellet’s microstructure and an increase in density and length of microcracks within vateritic pellets when higher pressing force was applied.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

10402 - Inorganic and nuclear chemistry

Projekt

<a href="/cs/project/GA17-05030S" target="_blank" >GA17-05030S: Vliv reakčních podmínek na vznik a mechanické vlastnosti polymorfů CaCO3 ve vápnitých stavebních materiálech</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the Second International Conference on Theoretical, Applied and Experimental Mechanics

ISBN

978-3-030-21893-5

ISSN

2522-560X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

3-8

Název nakladatele

Springer Nature

Místo vydání

Cham

Místo konání akce

Corfu

Datum konání akce

23. 6. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—