Evaluation of self-healing in concrete by means of analytical techniques

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F19%3A00511548" target="_blank" >RIV/68378297:_____/19:00511548 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Evaluation of self-healing in concrete by means of analytical techniques

Popis výsledku v původním jazyce

In the present work, the self-healing process in concrete was evaluated using analytical techniques. For this purpose, two concrete mixes of different composition (one used as reference) were prepared with a W/B of 0.45. The self-healing process was triggered by the introduction in the concrete mix of a commercial expansive admixture (calcium sulfo-aluminate), two dicarboxylic acids, and sodium carbonate salt. After 28 days curing in water, the specimens were artificially cracked (crack width ≈ 400 μm) and then again water-cured for 40 days until self-healing occurred. The progress of self-healing was investigated with a stereo-microscope at 40, 50 and 60 days. The efficiency of the process was evaluated using micro-Raman spectroscopy and X-ray micro-computed tomography (XmCT). Significant reduction in the crack width was observed as a result of filling the crack with calcite generated during the self-healing process. In some cases, the crack was completely healed. The experimental methodology used provided new insights into the evolution of the self-healing phenomenon in concrete.

Název v anglickém jazyce

Evaluation of self-healing in concrete by means of analytical techniques

Popis výsledku anglicky

In the present work, the self-healing process in concrete was evaluated using analytical techniques. For this purpose, two concrete mixes of different composition (one used as reference) were prepared with a W/B of 0.45. The self-healing process was triggered by the introduction in the concrete mix of a commercial expansive admixture (calcium sulfo-aluminate), two dicarboxylic acids, and sodium carbonate salt. After 28 days curing in water, the specimens were artificially cracked (crack width ≈ 400 μm) and then again water-cured for 40 days until self-healing occurred. The progress of self-healing was investigated with a stereo-microscope at 40, 50 and 60 days. The efficiency of the process was evaluated using micro-Raman spectroscopy and X-ray micro-computed tomography (XmCT). Significant reduction in the crack width was observed as a result of filling the crack with calcite generated during the self-healing process. In some cases, the crack was completely healed. The experimental methodology used provided new insights into the evolution of the self-healing phenomenon in concrete.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20102 - Construction engineering, Municipal and structural engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

26. konference Betonářské dny 2019. Sborník přednášek

ISBN

978-80-907611-2-4

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Česká betonářská společnost ČSSI

Místo vydání

Praha

Místo konání akce

Hradec Králové

Datum konání akce

20. 11. 2019

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—