Monitoring durability of limestone cement paste stored at conditions promoting thaumasite formation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F20%3A00535250" target="_blank" >RIV/68378297:_____/20:00535250 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.23967/dbmc.2020.098" target="_blank" >https://doi.org/10.23967/dbmc.2020.098</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.23967/dbmc.2020.098" target="_blank" >10.23967/dbmc.2020.098</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Monitoring durability of limestone cement paste stored at conditions promoting thaumasite formation
Popis výsledku v původním jazyce
The durability of Portland-limestone cement withhigh limestone content was monitored at conditions promoting thaumasite formation. Pore structure and deterioration characteristics were assessed with X-ray micro-computed tomography and correlatedwith material’s strength. Changes in crystalline and amorphous phasesof the cement paste were investigated with X-ray powder diffractionand solid state nuclear magnetic resonance spectroscopy. Rapid deterioration was observed, evolving as a front causingconcentric crack patterns followed by detachment of the part of specimen in contactwith the corrosive solution. Thisultimately led to loss of structural integrity after 4monthsofexposure.During sulfate attack, thaumasite, ettringite and gypsum formed at the expense of portlandite, calcite and monocarboaluminate hydrate. Furthermore, polymerization of silicate chains in C-S-H and deterioration of C-S-H also occurred.
Název v anglickém jazyce
Monitoring durability of limestone cement paste stored at conditions promoting thaumasite formation
Popis výsledku anglicky
The durability of Portland-limestone cement withhigh limestone content was monitored at conditions promoting thaumasite formation. Pore structure and deterioration characteristics were assessed with X-ray micro-computed tomography and correlatedwith material’s strength. Changes in crystalline and amorphous phasesof the cement paste were investigated with X-ray powder diffractionand solid state nuclear magnetic resonance spectroscopy. Rapid deterioration was observed, evolving as a front causingconcentric crack patterns followed by detachment of the part of specimen in contactwith the corrosive solution. Thisultimately led to loss of structural integrity after 4monthsofexposure.During sulfate attack, thaumasite, ettringite and gypsum formed at the expense of portlandite, calcite and monocarboaluminate hydrate. Furthermore, polymerization of silicate chains in C-S-H and deterioration of C-S-H also occurred.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GJ18-26056Y" target="_blank" >GJ18-26056Y: Experimentální kvantifikace a modelování degradace směsných cementových past s příměsí vápence vlivem síranové koroze za vzniku thaumasitu</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Current topics and trends on durability of building materials and components. Proceedings of the XV edition of the international conference on durability of building materials and components (DBMC 2020)
ISBN
978-84-121101-8-0
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
1039-1046
Název nakladatele
International Center for Numerical Methods in Engineering (CIMNE)
Místo vydání
Barcelona
Místo konání akce
Barcelona
Datum konání akce
20. 10. 2020
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—